Hydrothermal synthesis of CeO2 nano-particles
A.I.Y. Tok,F.Y.C. Boey,Z. Dong,X.L. Sun
DOI: https://doi.org/10.1016/j.jmatprotec.2007.02.042
IF: 6.3
2007-07-01
Journal of Materials Processing Technology
Abstract:Nano-crystalline particles of CeO2 have been synthesized via a low temperature hydrothermal synthesis process. Two types of precursors were studied—cerium hydroxide and ceria acetate. The precursors were adjusted to a basic (pH 10) and acidic (pH 4) medium before hydrothermal treatment at various durations of 6, 12, 18, and 24h at 250°C using a Teflon-lined hydrothermal bomb. The synthesized samples were characterized using DTA/TGA, XRD and TEM. Based on the characterization results, both precursor systems produced crystalline ceria nano-particles after 6h of hydrothermal synthesis at 250°C. The average crystallite sizes were 6 and 15nm for the hydroxide and acetate system, respectively. The acetate precursor system appeared to produce better particles in terms of crystallinity and morphology. Based on the DTA/TGA analysis, hydrothermal synthesis had been effective in reducing the amount of intermediate products. With increasing hydrothermal treatment duration of up to 24h, the samples did not exhibit a remarkable improvement in properties. The synthesized nano-particles were subsequently heat treated at 500 and 1000°C for 2h. After the heat treatment, enhanced crystallinity and growth in crystallite size was observed, but particles appeared more agglomerated.
materials science, multidisciplinary,engineering, manufacturing, industrial