Abstract:Cerium dioxide (CeO2) nanoparticles were synthesized by sol–gel-based hydrothermal method. During synthesis, cerium(III) chloride heptahydrate (CeCl3⋅7H2O) was used as cerium source; ammonia (NH3), tetraethylammonium hydroxide (C8H21NO), tetra-n-butyl ammonium hydroxide (C16H37NO), benzyl trimethyl ammonium hydroxide (C10H17NO) and benzyl triethyl ammonium hydroxide (C13H23NO) ionic liquids were used as catalyst, deionized water (H2O) was used as hydrolysis agent and solvent, and 2-aminopropanoic acid (C3H6NO2) was used as stabilizing agent. The nano-CeO2 particles were characterized by several techniques X-ray diffractometer (XRD), particle size analyzer, Branauer–Emmett–Teller analyzer (BET), ultraviolet–visible spectrophotometer (UV–Vis), transmission electron microscope (TEM). XRD characterization confirms that CeO2 crystals were analyzed as cubic fluorite structure. The full width at half maximum (FWHM) values referring to [111] lattice planes of CeO2 indicate a decrease in crystallinity associated with different bases used during synthesis of particles. Small sized crystals were formed in weak ionization degree and branched structures. As the crystallite size decreases, both agglomeration and the hydrodynamic diameter increases as expected. The size distribution of nano-CeO2 particles obtained by precipitation using different bases with a pH of 10 decreases from 25.92 to 20.57 nm. The size of nanoparticles prepared using ammonia at pH 9 and 8 are 15.60 and 9.50 nm, respectively. The most significant surface area change occurred in particles obtained using benzyl trimethyl ammonium hydroxide (BTMAH) and benzyl triethyl ammonium hydroxide (BTEAH). Such a significant reduction in surface area is believed to be due to the agglomeration or aggregation of particles with small crystallite size, resulting in smaller sized crystals as the alkyl group chain length and branching increase. These irregularities may result from the agglomeration and formation of large clusters observed by the TEM. The obtained CeO2 nanoparticles are crystalline and can readily be dispersed in water without any additional processing or surfactant agent. Well-defined strong absorbance peak located at 200–800 nm was observed for all samples. The bandgap increases with the decrease in particle size, meaning that smaller particles exhibit better UV absorption. The fact that the particles obtained in the presence of BTMAH and BTEAH cut off longer wavelength proved that it is due to lower bandgap energies.Graphical abstract

Size controlled synthesis of CeO2 nanoparticles by a microemulsion method

Controlled synthesis of Ce0.8Y0.2O1.9 nanoparticles by reverse microemulsion

Preparation and characterization of size-controlled CeO 2 nanoparticles coated with SiO 2

Synthesis of Cerium(IV) Oxide Ultrafine Particles by Solid‐State Reactions

Preparation and Characterization of Size-Controlled Ceo2 Nanoparticles Coated with Sio2

Characterization of CeO 2 Fine Particles Prepared by the Homogeneous Precipitation Method with a Mixed Solutionof Ethylene Glycol and Polyethylene Glycol

Preparation of nano-sized CeO2 by mechanochemical reaction of cerium carbonate with sodium hydroxide

Synthesis and characterisation of CeO2 nanoparticles and rods

Preparation of Nanometer Cerium Oxide by Microwave Irradiation and Study on Its Surface Modification

A Size-Controllable Precipitation Method to Prepare CeO2 Nanoparticles in a Membrane Dispersion Microreactor

Preparation and characterization of CeO2 with different particle sizes and morphology

Preparation and Characterization of CeO<sub>2</sub> with Different Particle Sizes and Morphology

Study of the Preparation and Properties of CeO2single/multiwall Hollow Microspheres

Planar-dependent oxygen vacancy concentrations in photocatalytic CeO2 nanoparticles

Preparation of ceria by combined sol–gel and hydrothermal method: insights from the effects of different bases on the particle size distribution

Sustainable and Facile Route to Nearly Monodisperse Spherical Aggregates of CeO2 Nanocrystals with Ionic Liquids and Their Catalytic Activities for CO Oxidation

Synthesis and Characterization of Nanoscaled Cerium (IV) Oxide Via a Solid‐State Mechanochemical Method

Controllable synthesis of nearly monodisperse spherical aggregates of CeO2 nanocrystals and their catalytic activity for HCHO oxidation.

Controllable synthesis of spherical cerium oxide particles

A New Method to Preparing Monodisperse CeO_2 Nanoparticles

Effects of PVP and CTAB surfactants on the morphology of cerium oxide nanoparticles synthesized via co-precipitation method