Abstract:Tungsten and tungsten alloys are widely used in high temperature environments where arc ablation or mechanical deformation and damage are the main sources of materials failure. For high temperature critical applications in thermomechanical environments, however, the low strength limits the use of tungsten and tungsten alloys. Hence, new tungsten based materials with good high temperature thermomechanical properties need to be developed in order to extend the use of tungsten. TiC particle-reinforced tungsten based composites (TiCp/W) were fabricated by hot pressing at 2000 °C, 20 MPa in a vacuum of 1.3×10−3 Pa. The composites were examined with respect to their thermophysical and mechanical properties at room temperature and at elevated temperature. Vickers hardness and elastic modulus increased with increasing TiC content from 0 to 40 vol.%. The highest flexural strength, 843 MPa, and the highest toughness, 10.1 MPam1/2, of the composites at room temperature were all obtained when 20 vol.% TiC particle were added. As the test temperature rose, the flexural strength of the TiCp/W composites firstly increased and then decreased, except in the monolithic tungsten. The highest strength of 1155 MPa was measured at 1000 °C in the composite containing 30 vol.% TiC particles. The strengthening effect of TiC particles on the tungsten matrix is more significant at high temperatures. With the addition of TiC particles, the thermal conduction of tungsten composites was drastically decreased from 153 Wm−1K−1 for monolithic W to 27.9 Wm−1K−1 for 40 vol.% TiCp/W composites, and the thermal expansion was also increased. The new composites are successfully used to make high temperature grips and moulds.

High-temperature response of TiC particulate reinforced titanium matrix composite

Elevated Temperature Mechanical and Thermophysical Properties of Titanium Carbide Particle-Reinforced Tungsten Composites

Strengthening Effect of in Situ Tic Particles in Ti Matrix Composite at Temperature Range for Hot Working

High-temperature Mechanical Properties and Strengthening Mechanism of In-situ (TiB+ TiC)/Ti-1100 Composite

Mechanical Properties and Strengthening Effects of in Situ (Tib+tic)/ti-1100 Composite at Elevated Temperatures

High-temperature Tensile Properties of in Situ-Synthesized Titanium Matrix Composites with Strong Dependence on Strain Rates

Thermomechanical Properties of TiC Particle-Reinforced Tungsten Composites for High Temperature Applications

Experimental Description of Thermomechanical Properties of Carbon Fiber-Reinforced Tic Matrix Composites

Elevated temperature strength of TiCp/W composites

Mechanical Properties and Strengthening Mechanisms of in Situ (Tib+tic)/ti-1100 Composite at Elevated Temperature

Compressive response and microstructural evolution of in-situ TiB2 particle-reinforced 7075 aluminum matrix composite

Temperature dependence of fracture behavior of in situ synthesized TiC/Ti-alloy matrix composite

Study on high temperature strengthening mechanism of TiB 2p/6061Al composite

The Influence of High Temperature and High Pressure on the Grain Sizes of In-situ Formed TiC Particulate Reinforcements in Ti Matrix Composites

The dynamic mechanical response of Al2O3 and TiB2 particulate reinforced aluminum matrix composites produced by in-situ reaction

Investigation on the High-Temperature Ductility and Fracture Mechanisms of an In-Situ Particle Reinforced Al Matrix Composite 7075Al/tib2

Study on Dynamic Compressive Mechanics Behavior of TC17 Titanium Alloy at High Temperature and High Strain Rates

High-temperature tensile strengths of in situ synthesized TiC/Ti-alloy composites

Mechanical Properties Of In Situ Synthesized Titanium Matrix Composites At Elevated Temperature

Effect of reinforcements on high temperature mechanical properties of in situ synthesized titanium matrix composites

The microstructure and elevated temperature strength of tungsten-titanium carbide composite