Effect of TiC Content on Microstructure and Mechanical Properties of High-temperature Titanium Matrix Composites
Zhang Changjiang,Lin Sibo,Zhang Shuzhi,Kong Fantao,Chen Yuyong
2017-01-01
Rare Metal Materials and Engineering
Abstract:A near a titanium alloys reinforced with different volume fraction of TiC, were prepared by vacuum induction melting. The addition of TiCp was lvol%, 2.5vol%, 5vol.%, 7.5vol%, 10vol%, 15vol%. Effect of TiC content on microstructure and mechanical properties of near a titanium alloys was systematically investigated by XRD, OM, SEM and Instron universal testing machine. The XRD result confirms that in situ casting process is feasible to fabricate the composite. As TiC content increases, the morphologies of TiC are transformed from long strip-like to equiaxed shape and then to dendritic characteristic, which is closely related to the solidification paths. The addition of TiC promotes the ultimate compression strength (UCS) and yield strength (YS) of the alloy. However, as the TiC content reaches to a certain degree, the strengths decrease in different degree. The increased.UCS and YS is accompanied by the rapid decrease in fracture strain.