Abstract:With the aim to investigate the effect of parameters and the quenching process on the joint microstructure and mechanical properties of hot stamping steel by laser welding, BR1500HS boron steel was welded by wire-filling laser welding with ER70-G welding wire under different parameters. The welded specimens were heated to 900 °C and held for 5 min before water quenching. A universal material test machine, optical microscope, Vickers hardness tester, scanning electron microscope, and electron backscatter diffraction (EBSD) were used to characterize. The results show that the heat input should be greater than 1040 J/cm and the optimal wire-feeding speed is between 160 cm/min and 180 cm/min. The tensile strength of the quenched joint can reach greater than 1601.9 MPa at compatible parameters. More retained austenite distributes in the fusion zone (FZ) and fine grain zone (FGZ) than the coarse grain zone (CGZ) before quenching. However, the retained austenite in FZ and heat-affected zone (HAZ) decreases clearly and distributes uniformly after quenching. The grain diameter in FZ before quenching is not uniform and there are some coarse grains with the diameter greater than 40 μm. After quenching, the grains are refined and grain diameter is more uniform in the joint. With the increase in heat input, the microhardness of FZ and HAZ before quenching decreases from 500 HV to 450 HV. However, if the wire-feeding speed increases, the microhardness of FZ and HAZ before quenching increases from 450 HV to 500 HV. After quenching, the joint microhardness of all samples is between 450 HV and 550 HV. The fracture morphology of the joint before quenching consists of a large number of dimples and little river patterns. After quenching, the fracture morphology consists of a large amount of river patterns and cleavage facets due to the generation of martensite.

Effect of Laser Hardening Parameters on the Valve Seat of Worm Cast Iron

Laser strengthening of air-cooled diesel engine phosphorus cast iron cylinder liner and its friction & wear properties

Effect Of Laser Melting Processing On The Microstructure And Wear-Resistance Of Gray Cast-Iron

Technique Principle of Laser Hardening Steeland Cast Iron

Microstructure and wear behavior of arc-shaped 40CrNiMo steel after laser hardening

Analysis of Laser Surface Hardening of GM246 Cast Iron

Exploring the influence and mechanism of hardfacing STL12 on impact wear performance at high temperature and heavy load

Microstructure and mechanical properties of composite strengthened high-chromium cast iron by laser quenching and laser shock peening

Effect of different hardness units on fatigue wear resistence of low hardenability steel

Investigation on Microstructure and Performance of Boron Cast IronCylinder Liner with Laser Remelting

Influence of multi-pass laser hardening of normalized AISI 4140 on the grain size

Effects of electrolyte on hardening in laser hole sealing of commercially pure grade 1 titanium

Microstructure Evolution and Mechanical Properties of AISI 430 Ferritic Stainless Steel Strengthened Through Laser Carburization

Effects on Microstructure and Properties of Brass Treated by Laser Shock Processing

Research of laser transformation hardening on mild steel

Effect of laser surface hardening on a low carbon steel substrate wear and hardness

Effect of Multi-Layer Laser Heating on the Microstructure and Microhardness of Laser Hot-Wire Deposited FV520B Steel

Study on Laser Surface Hardening Behavior of 42CrMo Press Brake Die

Study on laser surface hardening process of 30CrMnSiNi2A ultra-high strength steel fabricated by laser deposition manufacturing

Research on Parameters of Wire-Filling Laser Welding and Quenching Process for Joints Microstructure and Mechanical Property of BR1500HS Steel

Effect of laser remelting power on the microstructure and properties of vanadizing layer on AISI 52100 steel pin shaft