Abstract:In this work, amorphous thin films in Mg-Si-O-N system typically containing >15 at.% Mg and 35 at.% N were prepared in order to investigate especially the dependence of optical and mechanical properties on Mg composition. Reactive RF magnetron co-sputtering from magnesium and silicon targets were used for the deposition of Mg-Si-O-N thin films. Films were deposited on float glass, silica wafers and sapphire substrates in an Ar, N2 and O2 gas mixture. X-ray photoelectron spectroscopy, atomic force microscopy, scanning electron microscopy, spectroscopic ellipsometry, and nanoindentation were employed to characterize the composition, surface morphology, and properties of the films. The films consist of N and Mg contents up to 40 at.% and 28 at.%, respectively and have good adhesion to substrates and are chemically inert. The thickness and roughness of the films increased with increasing content of Mg. Both hardness (16–21 GPa) and reduced elastic modulus (120–176 GPa) are strongly correlated with the amount of Mg content. The refractive index up to 2.01 and extinction coefficient up to 0.18 were found to increase with Mg content. The optical band gap (3.1–4.3) decreases with increasing the Mg content. Thin film deposited at substrate temperature of 100 °C shows a lower value of hardness (10 GPa), refractive index (1.75), and higher values of reduced elastic modulus (124 GPa) as compared to the thin film deposited at 310 °C and 510 °C respectively, under identical synthesis parameters.

Influence of Substrate Temperature on Silicon Nitride Films Deposited by R.F. Magnetron Sputtering

Optical Properties Study of Silicon Oxynitride Films Deposited by RF Magnetron Sputtering

Deposition of Dense SiO2 Thin Films for Electrical Insulation Applications by Microwave ECR Plasma Source Enhanced RF Reactive Magnetron Sputtering

Thin films of silicon nitride deposited at room temperature by non-reactive magnetron sputtering: radiofrequency power and deposition time influence on the formation of α-Si3N4 and its optical properties

Influence of Substrate Temperature on Structural Properties and Deposition Rate of AlN Thin Film Deposited by Reactive Magnetron Sputtering

Influences of different sputtering current on the microstructure and electrical properties of silicon nitride thin films deposited on cemented carbide tools

Preparation of silicon carbide nitride thin films by sputtering of silicon nitride target

Optical & Electronic Properties of Carbon Nitride Thin Films

Growth and characterization of silicon nitride films for optoelectronics applications

Substrate Temperature Effect on Growth Behavior and Microstructure-Properties Relationship in Amorphous Ni-Nb Thin Films

Sputtering of aluminium nitride (002) film on cubic silicon carbide on silicon (100) substrate: influences of substrate temperature and deposition power

Characterization of silicon nitride films prepared by MW-ECR magnetron sputtering

Effects of deposition temperature on the mechanical and structural properties of amorphous Al-Si-O thin films prepared by RF magnetron sputtering

Spectra Characterization of Silicon Carbonitride Thin Films by Reactive Radio Frequency Sputtering

Effects of Substrate Temperature on the Properties of Silicon Oxide Films by PECVD

Analysis of active screen low temperature plasma-assisted deposition of iron nitride thin films on silicon (100) substrate

Optical and mechanical properties of amorphous Mg-Si-O-N thin films deposited by reactive magnetron sputtering

Influence of Sputtering Process on the Deposition and Optical Properties of Sicn Films

Low temperature growth of c-axis oriented AlN films on γ-LiAlO2 by radio frequency magnetron sputtering

MICROSTRUCTURE AND OPTICAL PROPERTIES OF SILICON NITRIDE THIN FILMS AS RADIATIVE COOLING MATERIALS

Effect of N2 reactive gas flow rate on the structural, optical and wettability properties of silicon carbon oxynitride thin films