Effect of Ca on Particulate Dispersion and Foam Stability in Gas Injection Foaming Process
LIU Xing-nan,LI Yan-xiang,CHEN Xiang,FAN Xue-liu
DOI: https://doi.org/10.19476/j.ysxb.1004.0609.2011.02.021
2011-01-01
The Chinese Journal of Nonferrous Metals
Abstract:The effect of Ca addition on particulate dispersion and foam stability in gas injection foaming process was investigated.The particulate size in the melt,the critical injection depth,the thickness of foam cell wall and the wetting angle of Al2O3 particulate on the bubble surface were viewed without and with Ca addition into A356 melt,respectively.The results show that the particulate size is smaller with addition of 1%(mass fraction) Ca.Thus,it’s easier to be dispersed for fine particulates with Ca addition.The critical injection depth of the melt becomes larger,so,the stability of aluminum foam becomes worse when adding calcium.The wetting angle of Al2O3 particulate on the bubble surface is about 65°,less than the ideal angle of 90°.With Ca,the wetting angle of the particulate decreases away from the ideal value.As a result,although the average size of the particulates decreases and the thickness of foam cell wall increases with Ca addition,the stability of the foam still becomes worse.