Abstract:The solidification microstructure of aluminum foams is evidently different from that of bulk aluminum alloys. Generally, a single α-Al grain runs through the entire thickness of a cell-wall, and the grain morphology is irregular. However, the formation mechanism of the special microstructure in aluminum foams is unclear now, and few studies focused on optimizing the microstructure. In this study, grain refinement of aluminum foams by increasing cooling rate and inoculation were carried out, and thermal analysis was used to measure and judge solidification of aluminum foams. Experimental results show that grain refinement can be achieved by the above two methods, and the latter is more effective. The nucleation undercooling of aluminum foams decreases with the increase of Al–5Ti–1B addition. Grains can be well refined even in thin cell walls after inoculation, and the grain morphology changes from irregular to equiaxed. Under the same conditions, α-Al grains of Al foams are smaller than those of the bulk Al alloy, either with or without inoculation. An anisometric growth model of α-Al grains in foamed aluminum melt restricted by surrounding bubbles is proposed. The model shows that: (1) the size of the inhibited nucleation zone (INZ) around growing grains decreases due to the high constitutional undercooling caused by solute enrichment in cell walls, thus grains in cell walls are smaller than those of bulk Al alloy; (2) under normal solidification conditions, the shape of the INZ is irregular. Grains in aluminum foams will replicate contours of cell walls or Plateau borders, presenting irregular shapes. Increasing cooling rates and/or inoculation can reduce the size of INZ and change its shape. The grain morphology will change from irregular to equiaxed under proper conditions.

Aluminium foam with sub-mm sized cells produced using a rotating gas injector

Short‐Range Ordered Aluminum Foams

The Cell Size Reduction of Aluminum Foam with Dynamic Gas Injection Based on the Improved Foamable Melt

Factors affecting the microstructure of a fine ceramic foam

Preparation of Aluminum Foam by Gas Injection Foaming

Study on an Aluminum Foam by Gas Injection Foaming

Properties of Aluminum Foam Prepared by Gas Injection Method

Factors Influencing Foam Height in Gas Injection Process for Aluminum Foams

Comparison of Aluminium Foams Prepared by Different Methods Using X-ray Tomography

Solidification microstructure and grain refinement of closed-cell aluminum foams

The influence of pure Al and hypoeutectic Al Si alloy base materials on the cell structures of aluminum foams produced by gas injection foaming process

Compressive Performance and Deformation Mechanism of the Dynamic Gas Injection Aluminum Foams

The Stability of Aluminum Foams at Accumulation and Condensation Stages in Gas Injection Foaming Process

Development of AlMg35-TiH2 composite foaming agent and fabrication of small pore size aluminium foams

Fabrication of Uniform and Rounded Closed-Cell Aluminum Foams Using Novel Foamable Precursor Particles (FPPs)

Aluminum Foam Sandwich: Pore Evolution Mechanism Investigation and Engineering Preparing Optimization

Influence of Gas Pressure and Blowing Agent Content on the Formation of Aluminum Alloy Foam

Bubble Formation at a Submerged Orifice in High-Speed Horizontal Oscillation

Bubble Formation at a Submerged Orifice for Aluminum Foams Produced by Gas Injection Method

Comparison of Cell Wall Microstructure of Aluminum Foams Produced by Melt Foaming and Gas Injection Foaming Processes

Inner Voids of Octavinyl Polyhedral Oligomeric Silsesquioxane Acting as Cell Embryos for Polymer Foaming