Growth, structure, and stability of Au on ordered ZrO2(111) thin films

Yonghe Pan,Yan Gao,Guodong Wang,Dandan Kong,Liang Zhang,Jianbo Hou,Shanwei Hu,Haibin Pan,Junfa Zhu

DOI: https://doi.org/10.1021/jp201960t

2011-01-01

Abstract:The growth, electronic properties, and thermal stability of Au nanoparticles on ordered ZrO2(111) thin film surfaces were investigated by low-energy electron diffraction (LEED), X-ray photoelectron spectroscopy (XPS), and synchrotron radiation photoemission spectroscopy (SRPES). The thin ZrO2(111) films were grown on a Pt(111) substrate. At room temperature, Au initially grows as 2D islands on the ZrO2(111) thin films up to 0.1 ML, followed by 3D growth with a number density of similar to 1.4 x 10(12) particles/cm(2). The binding energy of the Au 4f peaks shifts monotonically toward a higher binding energy with decreasing the Au particle size by 0.4 eV, which can be attributed to the contribution from both the initial- and final-state effects. Au atoms most likely form Au delta- initially and become metallic states as the coverage increases. Thermal annealing experiments demonstrate that Au particles experience significant sintering before desorption from the ZrO2(111) surface. In addition, Au particles are more thermally stable on the sputtered ZrO2(111) surface than on the pristine ZrO2(111) surface due to the stronger bonding of Au atoms on the surface defect sites. Moreover, large Au particles are more thermally stable than small ones on the ZrO2(111) surface.