An Investigation Of The Ordered Au/Cu(111) Surface - Leed, Araes And Arups Results

R. Xu,S. Bao,G. Liu

DOI: https://doi.org/10.1016/0039-6028(90)90565-P

IF: 1.9

1990-01-01

Surface Science

Abstract:A (2 × 1)/(1 × 2) ordered structure prepared by vapor deposition of Au onto Cu(111) and subsequent heating has been characterized by means of LEED, ARAES and ARUPS. ARAES analysis shows a Au content of 55% and 50% in the first two layers, respectively, using pure Au and Cu for calibration. This suggests that a mixed (2 × 1) and (1 × 2) structure with co-planar Au and Cu atoms exists on the top layer corresponding to CuAu(111) rather than Cu 3 Au(111). It is also inferred from the ARAES analysis that the top layer is rippled with the Au atoms about 0.4 Å higher than the Cu atoms. Au-induced features at about 6.5 and 5.9 eV below the Fermi level are observed from the ARUPS using He I, and their dispersion along the [11̄0] and the [112̄] directions is also determined. After evaporating two or more layers of Au atoms on Cu(111), as indicated by measurement of ARAES, LEED shows epitaxial hexagonal Au layers with a nearest-neighbor spacing of pure Au.