Preparation of precipitated silica from desilicated solution of high-alumina fly ash by dissolution with alkali: experiment and principle of polymerization of silicic acid

Ge LI,Hongwen MA,Hao LIU,Dan ZOU

DOI: https://doi.org/10.3969/j.issn.0438-1157.2011.12.041

2011-01-01

Abstract:In this paper, high-alumina fly ash from a thermal-electric plant of Shaanxi Province was used as raw material, and was treated with alkali to prepare desilicated solution, which was then carbonated to prepare precipitated silica. During orthogonal experiments and single-factor experiments, the optimal carbonation conditions were determined as follows, under 100 r·min -1 speed stirring, 500 ml·min -1 CO 2 flow rate, sodium metasilicate concentration 17.8°Bé, and at reaction temperature around 85°C, reaction time around 2.5 h. The white carbon black product (BTH-01) was prepared from silica gel through drying at 105°C overnight. The product (BTH-01) satisfied the type A standard of white carbon black GB10517-89. The carbonation reaction process was analyzed. Nuclear magnetic resonance measurement method was used to trace the processing path of silica gel, which could better describe the Si-O conjugation during different times in carbonation. The technology provides some guidance to analyzing the structure of white carbon black. © All Rights Reserved.