Abstract:We analyze progressive damage and failure of composite laminates by using a micromechanical bridging model and compare numerical and experimental results for three fracture problems, namely, the four-point bending, the simple tension, and the simple tension of a laminate with an open hole at its centroid. These problems involve fiber–matrix interface debonding, constituents’ damage, interlayer delamination, and localized damage due to stress concentration. Macroscopic constitutive equations of unidirectional lamina, derived from those of the fiber and the matrix by using the bridging model with the fiber material assumed to be linearly elastic and the matrix to be elasto-plastic obeying the Drucker–Prager yield criterion, are employed. Strains in each constituent of the composite are assumed to be infinitesimal for the additive decomposition of strains into elastic and plastic parts to be valid, and the incremental plasticity theory is used. Stresses in the two constituents are found from their values in the homogenized material by using a dehomogenization technique. The intra-layer damage is assumed to initiate at a material point when the failure criterion for either the fiber or the matrix is satisfied. Young’s modulus of a constituent is degraded by following a Weibull distribution. A finite element is deleted when an energy-based failure criterion is satisfied in it, and the analysis is continued till the structure fails. The delamination between adjacent plies is simulated by including a thin resin layer at the interface and studying failure initiation and propagation in it. The computed reaction force versus the displacement curves and the failure patterns in the three problems are found to agree with the corresponding experimental data.

Micromechanical experiments of interlaminar deformation and damage in angle-ply thermoplastic composite laminates

Micromechanical Experiments of Interlaminar Deformation and Damage in Quasi-Isotropic Thermoplastic Composite Laminates

Micro Failure Analysis of Fiber Metal Laminates

Concurrent Multiscale Modeling of In-Plane Micro-Damage Evaluation in Z-pinned Composite Laminates

New Method on Experimental Damage Study of As4/Peek Composite Laminates

Interlaminar Stress and Damage Mechanism of Thermoplastic Composite Laminates

Microscopic Progressive Damage Simulation and Scale-Span Analysis of Cross-Ply Laminate Based on the Elastic–Plastic Theory

3D Elastic-Plastic Analysis and Experiment of Free Edge Effects in Angle-Ply Thermoplastic Composite Laminates

Compressive Experiment and Damage Simulation of A Composite Structure with Ply Drop-Off

Deformation and Fracture Mechanisms of Automated Fiber Placement Pre-Preg Laminates under Out-of-plane Tensile Loading

Investigation of Damage to Thick Composite Laminates under Low-Velocity Impact and Frequency-Sweep Vibration Loading Conditions

Numerical Elastic-Plastic Simulation of Interlaminar Stresses in a Notched Angle-Ply Thermoplastic Composite Laminate

Delamination Propagation Manipulation of Composite Laminates under Low-Velocity Impact and Residual Compressive Strength Evaluation

Experimental and FEM study on bearing mechanism of spliced ply with misalignment seams

Micro-mechanical Analysis of Matrix Crack-Induced Delamination in Cross-Ply Laminates in Tension

Micromechanical Progressive Damage Analysis of Inter- and Intra-Layer Failures in Fiber-Reinforced Composite Laminates

Measurements of interlaminar deformation in the composite laminates

Angle-ply orientation-dependent failure behaviors of carbon fiber reinforced polymer laminates

Damage Evolution and Multi-Scale Analysis of Carbon Fiber-Reinforced Cross-Ply Laminate with Thermal Residual Stress

A Micromechanical Failure Study of As(4)/Peek Composites

Micromechanical Modeling of Impact Damage Mechanisms in Unidirectional Composite Laminates