Abstract:The dynamic mechanical behavior of thermoplastic composites over a wide range of strain rates has become an important research topic for extreme environmental survivability in the fields of military protection, aircraft safety, and aerospace engineering. However, the dynamic compression response in the out-of-plane direction, which is one of the most important loading conditions resulting in the damage of composite materials, has not been investigated thoroughly when compared to in-plane compression and tensile behavior under high strain rates. Thus, we used split Hopkinson pressure bar (SHPB) tests to conduct the out-of-plane compression test of cross-ply carbon fiber-reinforced polyetheretherketone (AS4/PEEK) composite laminates. Afterward, the damage mechanism under different strain rates was characterized by the macrostructure morphologies and scanning electron microscope micrographs. Two major cases of the incomplete failure condition and complete failure condition were discussed. Dynamic stress-strain curves expound the strain rates dependencies of elastic modulus, failure strength, and failure strain. An obvious spring-back process could be observed under incomplete failure tests. For the complete failure tests, secondary loading could be observed by reconstructing and comparing the dynamic response history. Lastly, various failure modes that occurred in different loading strain rates illustrate that the damage mechanism also shows obvious strain rate sensitivity.

Interlaminar Stress Analysis of Thick Thermoplastic AS4-PEEK Composite Laminates

Interlaminar Stress and Damage Mechanism of Thermoplastic Composite Laminates

The Three-dimensional Elastic-plastic Analysis of Interlaminar Stresses in Notched Thermoplastic Composites

Strain-rate Dependence of Interlaminar Stress Fields in the Vicinity of Free Edges of AS4-PEEK Composite Laminates Under Uniaxial Tension

Three-Dimensional Elastic-Plastic Analysis of the Interlaminar Stresses for the AS4/PEEK Composite Laminate with a Circular Hole

Viscoplastic Analysis of the Off-axis Rate-dependent Inelastic Behavior of Unidirectional AS4/PEEK

Numerical Elastic-Plastic Simulation of Interlaminar Stresses in a Notched Angle-Ply Thermoplastic Composite Laminate

Three Dimensional Elasto-Plastic Stress Analysis of Thermo-Plastic Composites with a Hole

INTERLAMINAR STRESS ANALYSIS OF COMPOSITE LAMINATES SUBJECTED TO IN-PLANE LOADING

Viscoplastic Finite Element Method for Thermoplastic Composites

Effects of the Strain Rate Variation on the Interlaminar Stresses of the Thick Angle-Ply Laminates

Viscoplastic Analysis of the Off-axis Rate-dependent Inelastic Behavior of Unidirectional AS4/PEEK

Numerical Prediction of Elastic-Plastic Constitutional Behaviour of Thermoplastic Composites

The Out-of-Plane Compression Behavior of Cross-Ply AS4/PEEK Thermoplastic Composite Laminates at High Strain Rates.

A Phenomenological Intra-Laminar Plasticity Model for FRP Composite Materials

An Improved Analytical Solution For Process-Induced Residual Stresses And Deformations In Flat Composite Laminates Considering Thermo-Viscoelastic Effects

3D Stress Analysis of Composite Laminate Based on a Kind of Interfacial Element

Fracture Characters and Damage Mechanism of the Notched AS4/PEEK Composite Laminate

Micromechanical Modeling of Viscoplastic Behavior of Laminated Polymer Composites with Thermal Residual Stress Effect

Micromechanical Modeling on the Rate-Dependent Viscoplastic Behavior of Polymer Composites with Thermal Residual Stress Effect

Mechanical behavior in bending deformation of thermoplastic composite laminates with different stacking sequences