Investigation on structural, dielectric, ferroelectric, and piezoelectric properties of (1 − x)PbTiO3–(x)Bi(Zn2/3Nb1/3)O3 solid solutions
P. Aravinthkumar,G. Gopi,G. Anandha babu
DOI: https://doi.org/10.1007/s10854-024-11929-6
2024-01-23
Journal of Materials Science Materials in Electronics
Abstract:Single phase (1 − x ) PbTiO 3 − ( x )Bi(Zn 2/3 Nb 1/3 )O 3 ( x = 0.26, 0.28, 0.30, and 0.32) binary piezoceramics were prepared using solid-state reaction technique. Rietveld analysis confirms the tetragonal phase with P 4mm space group for all the compositions studied. The lattice parameters and unit cell volume are shown to increase with increasing Bi(Zn 2/3 Nb 1/3 )O 3 (BZN) substitution in PbTiO 3 (PT). The microstructure of the samples exhibit average grain size distribution (< 10 μm). Energy-dispersive X-ray spectroscopy (EDX) and X-ray Fluorescence (XRF) analysis confirmed the chemical composition of the prepared samples. Temperature and frequency-dependent dielectric studies revealed normal ferroelectric behavior in (1 − x )PT − ( x )BZN. High remnant polarization and saturation polarization were attained for 0.74PT − 0.26BZN samples. The Curie temperature ( T c ), dielectric constant ( ε r ), and remnant polarization decrease with increasing BZN substitution. The recoverable energy-storage density ( J reco ) of 0.2105 J/cm 3 and efficiency ( ɳ ) of 67% were achieved for 0.74PT–0.26BZN and 0.68PT − 0.32BZN ceramics, respectively. The enhanced piezoelectric coefficient charge d 33 − 409 pC/N was observed for 0.74PT – 0.26BZN. This study provides the route for exploring new piezoelectric materials with enhanced electrical properties.
engineering, electrical & electronic,materials science, multidisciplinary,physics, condensed matter, applied