Abstract:Recently, low-cost advanced high strength steels (AHSS) with high toughness and fatigue limit have been developed in order to ensure the safety and lightweight of the engineering components. As promising candidates for next generation of AHSS, the bainite/martensite multiphase high strength steels exhibit excellent combination of strength and toughness due to the refined multiphase microstructure and retained austenite films located between bainitic ferrite laths. The previous works showed that the mechanical properties of bainite/martensite multiphase steels can be further improved through quenching-partitioning-tempering (Q-P-T) process. In the present work, the effect of Q-P-T process on the microstructure and fatigue behaviors of steels was investigated, and the relationship between the microstructure and the fatigue crack propagation was discussed in detail. Here, a 20Mn2SiCrNiMo bainite/martensite multiphase steel was treated by Q-P-T processes: (1) quenching to 200 degrees C, partitioning at 280 degrees C for 45 min and finally tempering at 250 degrees C for 2 h (QPT200 sample); (2) quenching to 320 C, partitioning at 360 degrees C for 45 min and finally tempering at 250 degrees C for 2 h (QPT320 sample). Microstructure observations showed that the QPT200 sample consisted of leaf-shaped bainite, martensite and filmy retained austenite (RA), while some blocky martensite/austenite (M/A) islands were observed in QPT320 sample. The volume fractions of retained austenite in QPT200 and QPT320 samples are 4.5% and 9.8%, respectively. The fatigue crack propagation rate da/dN and threshold value of fatigue cracking Delta K-th were measured using compact-tensile specimens. The results showed that the Q-P-T process parameters had a significant influence on the microstructures and fatigue properties of the bainite/martensite multiphase steels. The bainite/martensite multiphase steel after appropriate Q-P-T treatment (QPT 200 sample in the present work) has higher Delta K-th and lower da/dN, which originates from the resistance on fatigue crack propagation due to the presence of leaf-shaped bainite and nanometer-sized retained austenite films. Furthermore, although the volume fraction of retained austenite in QPT320 sample is higher than that in QPT200 sample, the Delta k(th),h of QPT 320 sample is lower than that of QPT200 sample. It is suggested that the effect of retained austenite on the fatigue behaviors depends on its volume fraction, size and morphology.

High-cycle fatigue properties of microalloyed medium carbon steels with different oxygen content

Low Cycle Fatigue Properties and Fracture Mechanism of Q345qC Steel and Its Welded Joint

High-Cycle Fatigue Properties of Medium-Carbon Microalloyed Forging Steels

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

Abnormal Relation Between Tensile and Fatigue Strengths for a High-Strength Low-Alloy Steel

Study of the relationship among total oxygen, inclusions and fatigue properties of gear steel

Fatigue Behaviour of a Multiphase Medium Carbon Steel: Comparison Between Ferrite/pearlite and Tempered Microstructures

The fatigue properties, microstructural evolution and crack behaviors of low-carbon carbide-free bainitic steel during low-cycle fatigue

Fatigue Fracture Behavior of High Strength Cr-Mo-V Steel

FATIGUE BEHAVIOR OF BAINITE/MARTENSITE MULTIPHASE HIGH STRENGTH STEEL TREATED BY QUENCHING-PARTITIONING-TEMPERING PROCESS

High cycle fatigue behavior of titanium microalloyed high-strength beam steels

Effect of Oxygen Variation on High Cycle Fatigue Behavior of Ti-6Al-4V Titanium Alloy

Effect of Vanadium on the Fatigue Properties of Microalloyed Medium-Carbon Steels

Comparative Study of High-Cycle Fatigue and Failure Mechanisms in Ultrahigh-Strength CrNiMoWMnV Low-Alloy Steels

The correlation between martensite-austenite islands evolution and fatigue behavior of SA508-IV steel

Influence of Microstructure on Low-Cycle and Extremely-Low-Cycle Fatigue Resistance of Low-Carbon Steels

Very High Cycle Fatigue Behaviour of 2000‐mpa Ultra‐high‐strength Spring Steel with Bainite–martensite Duplex Microstructure

Microstructure and Mechanical Properties of Multi-Pass Forged and Annealed 42crmo Steel

Low-Cycle Fatigue Properties of P92 Ferritic-Martensitic Steel at Elevated Temperature