FATIGUE BEHAVIOR OF BAINITE/MARTENSITE MULTIPHASE HIGH STRENGTH STEEL TREATED BY QUENCHING-PARTITIONING-TEMPERING PROCESS

Gui Xiaolu,Zhang Baoxiang,Gao Guhui,Zhao Ping,Bai Bingzhe,Weng Yuqing
DOI: https://doi.org/10.11900/0412.1961.2015.00660
IF: 1.797
2016-01-01
ACTA METALLURGICA SINICA
Abstract:Recently, low-cost advanced high strength steels (AHSS) with high toughness and fatigue limit have been developed in order to ensure the safety and lightweight of the engineering components. As promising candidates for next generation of AHSS, the bainite/martensite multiphase high strength steels exhibit excellent combination of strength and toughness due to the refined multiphase microstructure and retained austenite films located between bainitic ferrite laths. The previous works showed that the mechanical properties of bainite/martensite multiphase steels can be further improved through quenching-partitioning-tempering (Q-P-T) process. In the present work, the effect of Q-P-T process on the microstructure and fatigue behaviors of steels was investigated, and the relationship between the microstructure and the fatigue crack propagation was discussed in detail. Here, a 20Mn2SiCrNiMo bainite/martensite multiphase steel was treated by Q-P-T processes: (1) quenching to 200 degrees C, partitioning at 280 degrees C for 45 min and finally tempering at 250 degrees C for 2 h (QPT200 sample); (2) quenching to 320 C, partitioning at 360 degrees C for 45 min and finally tempering at 250 degrees C for 2 h (QPT320 sample). Microstructure observations showed that the QPT200 sample consisted of leaf-shaped bainite, martensite and filmy retained austenite (RA), while some blocky martensite/austenite (M/A) islands were observed in QPT320 sample. The volume fractions of retained austenite in QPT200 and QPT320 samples are 4.5% and 9.8%, respectively. The fatigue crack propagation rate da/dN and threshold value of fatigue cracking Delta K-th were measured using compact-tensile specimens. The results showed that the Q-P-T process parameters had a significant influence on the microstructures and fatigue properties of the bainite/martensite multiphase steels. The bainite/martensite multiphase steel after appropriate Q-P-T treatment (QPT 200 sample in the present work) has higher Delta K-th and lower da/dN, which originates from the resistance on fatigue crack propagation due to the presence of leaf-shaped bainite and nanometer-sized retained austenite films. Furthermore, although the volume fraction of retained austenite in QPT320 sample is higher than that in QPT200 sample, the Delta k(th),h of QPT 320 sample is lower than that of QPT200 sample. It is suggested that the effect of retained austenite on the fatigue behaviors depends on its volume fraction, size and morphology.
What problem does this paper attempt to address?