Abstract:We herein report our investigation into the influence of cold-rolling on the recrystallization texture of the Zr-1Sn-0.3Nb-0.3Fe-0.1Cr alloy during annealing. The as-received plates were cold-rolled at 25 °C with different reductions of 6, 10, 14, 18, 30, 40, 50 and 70%. All cold-rolled sheets were annealed at 580 °C for 3 h, while 14 and 30% cold-rolled samples were also annealed at 580 °C for 12 h. The microstructures of the annealed samples were characterized by scanning electron microscopy (SEM) and electron backscatter diffraction (EBSD). Abnormal grains growth with about 23 μm in size appeared in the samples with 14% reduction and annealed at 580 °C for 3 h, which corresponded to the critical degree of alloy deformation. The texture of the 14% cold-rolled sheet was typical rolling texture <0001>//ND, after annealing, cold rolling texture was still retained. While the texture of the 30% cold-rolled sheet was <112¯0> parallel to the rolling direction (<112¯0>//RD), which changed to the recrystallization texture <0001>//ND, <101¯0>//RD and <112¯0>//RD characteristics after annealing. The loading direction is along the rolling direction (RD), the slip system and the Schmid factor are analyzed to more deeply understand and evaluate the plasticity of further rolling or punching. When the loading direction is along the rolling direction (RD), the predominant slip systems of annealed 14% reduction samples was prismatic and pyramidal plane system, and the annealed 30% reduction samples were prismatic with a pyramidal plane system. This implies that the use of 30% cold-rolled reduction and annealing at 580 °C for 12 h imparts a superior plasticity to the alloy, which may allow its application in future deformations, such as rolling or punching.

Texture gradient in rough-rolled plate of aluminum alloy 3104 and its effect on annealing textures evolution after hot compression

Evolution of Microstructures and Textures of High Purity Aluminium During Rolling and Annealing

Deformation and Recrystallization Textures in Straight-Rolled and Pseudo Cross-Rolled AA 3105 Aluminum Alloy

Texture Evolution in an Al-Cu-Mg Alloy During Hot Rolling

Textures Variation of 3104 Aluminum Alloy Sheets under Different Rolling Conditions

Shear Texture Gradient in Aa6061 Aluminum Alloy Processed by Accumulative Roll Bonding with High Roll Roughness

Study of Texture in 6016 Aluminum Alloy During Processing

Recovery of heavily cold-rolled aluminum: Effect of local texture

Evolution of texture and microstructure of 2E12 aluminum alloy during cold rolling and annealing

Evolution of Microstructure and Texture During Recovery and Recrystallization in Heavily Rolled Aluminum

Development of Microstructures and Texture During Cold Rolling in AA 7055 Aluminum Alloy

Evolution of texture during hot rolling of aluminum borate whisker-reinforced 6061 aluminum alloy composite

Texture evolution during multi-pass cold rolling and annealing of Ti-2Al-1.5Mn alloy

Texture, Microstructure and Mechanical Properties of 6111 Aluminum Alloy Subject to Rolling Deformation

Micro-mechanism of Texture Evolution During Isochronal Annealing of As-Annealed Hot Rolled Al-Cu-Mg Sheet

Effect of rolling geometry on the mechanical properties, microstructure and recrystallization texture of Al-Mg-Si alloys

B13-O-06Evolution of Texture in 6016 Aluminum Alloy During Processing

Unusual through-thickness variations of microstructure and texture in heavily rolled and annealed Al–0.3%Cu

Texture Evolution of Extruded AZ31 Magnesium Alloy Sheets

Texture Evolution of Cold-Rolled Zr-1Sn-0.3Nb-0.3Fe-0.1Cr Alloy During Annealing

Texture Evolution of Al-Zn-Mg-Cu Aluminum Alloy Plate During Cold Rolling