Ferroelectricity and Ferromagnetism of La0.5Lu0.5Ni0.5Mn0.5O3thin Films on Nb:SrTiO3substrates

S. Z. Li,C. Zhu,Z. B. Yan,S. J. Luo,K. F. Wang,J-M Liu

DOI: https://doi.org/10.1088/0953-8984/22/20/206005

2010-01-01

Abstract:Epitaxial orthorhombic La(0.5)Lu(0.5)Ni(0.5)Mn(0.5)O(3) (LLNMO) thin films deposited on Nb:SrTiO(3) (NSTO) substrates are prepared by pulsed laser deposition and their ferroelectricity and magnetism are investigated using various techniques. It is revealed that the as-prepared thin films are ferromagnetic (FM) insulators. The FM transition occurring at ∼ 125 K is evidenced by the well defined hysteresis at low temperature, with a saturated magnetic moment as high as 1.8 µ(B)/f.u. at ∼ 5 K. A reversible ferroelectric polarization of ∼ 0.2 µC cm(-2) below ∼ 140 K is also observed. The magnetism can be understood by the FM ordering associated with a partially ordered major Ni(2 +)-Mn(4 +) plus minor Mn(3+)-Ni(3+) configuration, while the ferroelectricity is argued to originate from the A-site disordering of La(3+) and Lu(3+).