Crystallization of aluminosilicate glass with additive TiO2
AM Hu,KM Liang,F Peng,H Shao,F Zhou,G Wang
2003-01-01
Rare Metal Materials and Engineering
Abstract:The crystallization of Li2O-CaO-MgO-Al2O3-Sio(2) (LCMAS) glasses doped with TiO2 (4%-12%) were investigated by differential thermal analysis (DTA), X-ray diffraction (XRD) and scanning electron microscopy (SEM). After a two-stage heat treatment, the phases such as beta-eucryptite, beta-spodumene and diopside were identified. The DTA curves showed a singe exothermic crystallization peak, and the glass transition temperature and the crystallization temperature decreased with increasing TiO2, while the values of crystallization activation energy and Avrami parameter (n) change with a parabolic trend from 424 +/- 5 kJ/mol, 1.3 (glass containing 4 wt.% TiO2) to 378 +/- 3 kJ/mol, 2.5 +/- 0.2 (glass containing 9 wt.% TiO2), and then to 399 +/- 3 kJ/mol, 2.1 +/- 0.2 (glass containing 12 wt.% TiO2). The microstructure of the glass-ceramic materials transformed from coarse fibrous with the direction to the surface to fine microstructure with less developed fibrous first, then to reverse. The results reveal that with increasing of TiO2 the glass system transforms from surface to the bulk crystallization, then to surface again.