Abstract:Nano-scaled pure and iron doping Titanium Dioxide prepared by TiCl4 hydrolysis were obtained. Two methods, step precipitation and co-precipitation, were applied in preparing the iron doping samples. The crystallization and decomposition processes were extensively investigated by methods of X-ray diffraction and TEM. The grain sizes under series of calcinating temperatures were computed according to Voigt function analysis. The results of TEM images also justified the computed grain size. The results showed that Titanium Dioxide prepared by TiCl4 hydrolysis is amorphous, and that no obvious: crystallization temperature or exothermic peaks were observed, contrary to the some previous reports. The computation applying the nuclei growth equation showed that the crystal grain growth of the pure and co-precipitation samples can be divided into 2 steps. The growth activation energy of the former step is 10.7kJ . mol(-1) and 8.6kJ . mol(-1), respectively and that of the latter step is 111.6kJ . mol(-1). As to the step precipitation samples, there showed no obvious difference in crystal growth activation energies for the 2 steps, and for the transformation of anantase to rutile was almost completed before 600 degrees C. There was evidence that the iron doping accelerated the transformation of rutile to anatase and this is especially obvious in step precipitation samples.

Crystallization behavior of LiNO3-doped TiO2 films prepared by sol-gel process

Crystallization behavior of LiNO3-doped SiO2-TiO2 films prepared through sol-gel method

Preparation of Li+-Doped Tio2 Films by Sol-Gel Process

Crystallization Behavior of Li+-Doped Sio2-Tio2 Films Prepared by Sol-Gel Dip Coating

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Influence of Iron Dopant on Crystallization and Photo-Induced Hydrophilicity of TiO2 Thin Films

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

The Thermal Analysis, Crystal Growth And Structure Transformation Of Nano-Scale Tio2 Prepared By Ticl4 Hydrolysis

Crystallization Kinetics of Li+-Doped TiO2 Films Prepared by Sol-Gel Dip Coating

Crystallization Behavior and Hydrophilic Performances of V2O5–TiO2 Films Prepared by Sol–gel Dip-Coating

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

The Characterization And Preparation Of Nano-Scale Fe Doping Tio2 By Sol-Gel Method - (Ii) - The Crystal Character And Grain Growth Of Fe Doping Tio2 Xerogel Powders

Preparation and Crystallization Behavior of SiO2-TiO2 Photo-Catalytic Films

Fabrication and Optical Property Study of TiO2 Nanocrystalline Films by Sol-gel Methods

The Preparation of TiO_(2-x)N_x(0<x<1) Thin Films by Sol-Gel Method and Its Photocatalysis and Hydrophilic Properties

Effect of Nb Doping Concentration on Transparent Conductivity of TiO2 Films Fabricated by Sol-Gel Method

Crystallization Behavior of Mg-Doped Titania

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Photo catalytic activity of Li+, Sb3+-Codoped TiO2 powders prepared through sol-gel method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature