Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Preparation of Mg2+-doped TiO(2)Thin film and its photocatalytic activity

Crystallization Behavior of Mg-Doped Titania

Mesoporous MgTa 2o 6 thin films with enhanced photocatalytic activity: On the interplay between crystallinity and mesostructure

Preparation and Structural Analysis of TiO2 Photocatalytic Film Modified by Triethylamine

P-doped TiO2 Immobilized Diatomite and Its Photocatalytic Performance under Visible Light

Preparation of Metallic Ion-Doped TiO2 Thin Films and Their Photocatalytic Performance for Toluene Degradation

Preparation and Photocatalytic Properties of Mo-doped TiO2

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Preparation of Lif-Doped Tio2 and Its Photocatalytic Performance for Degradation of Methylene Blue

Effect of the P/Ti Ratio on the Visible-Light Photocatalytic Activity of P-Doped Tio2

Effects of Germanium Doping on the Microstructure and Photoelectrochemical Properties of TiO2 Films by Sol-Gel Method

PREPARATION OF IRON-DOPED TITANIA NANOCRYSTALLINE GRAINS AND ITS PHOTOCATALYTIC PROPERTY

Photocatalitic Activity of N-doping TiO2 Thin Films Deposited by the Sol-Gel Technique

Fabrication of V-Doped TiO2 Nanoparticles and Photocatalytic Studies under Visible Light

Preparation of nano Eu3+-doped TiO2 and its photocatalytic degradation of methyl blue solution

Preparation and Crystallization Behavior of SiO2-TiO2 Photo-Catalytic Films

Effect of Mg and Cu co-doping on nanostructured TiO2 photocatalytic activity

The Chemical States and Properties of Doped TiO2 Film Photocatalyst Prepared Using the Sol–Gel Method with TiCl4 As a Precursor

Effect of Fe doping on crystalline phase, structure and photocatalytic properties of TiO2 thin films

Photo catalytic activity of Li+, Sb3+-Codoped TiO2 powders prepared through sol-gel method

Effects of Nd-doping on crystal phase, structure and photocatalytic performance of TiO 2 powders prepared by sol-gel method