Abstract:The aim of this research work is to optimize the synthesis of Li4SiO4 by a solid state method to maximize CO2 capture. This includes evaluating the main characteristics of the synthesised material which enhance the CO2 uptake performance. Starting from Li2CO3 and SiO2 pure reagents, the effect of the sintering process conditions (heating rate, synthesis temperature and holding time) of the previously mixed powders has been studied. The samples were characterized by N2 physisorption, particle size distribution and X-ray diffraction. The evaluation of the CO2 uptake performance of the samples has been carried out at 600 °C using a thermobalance under a flow of almost pure CO2. Unreacted Li2CO3 is present at low synthesis temperatures, and its content in the synthesised material decreases when higher temperatures are used, so complete conversion to Li4SiO4 is reached at 900 °C. At this temperature, the maximum CO2 uptake was found to be 20%, although it was yet far from the stoichiometric CO2 uptake value of 36.7%. The holding time at a synthesis temperature of 900 °C was then varied and a maximum CO2 uptake of 30.5% was obtained for a holding time of 2 h. Finally, under the optimised synthesis temperature and holding time conditions, the heating rate was varied. A value of 5 °C min−1 was found as the optimum one as the use of either lower or higher heating rates has a negative effect on the CO2 uptake performance. As crystalline phases, the particle size and BET surface area were very similar among all the prepared samples at 900 °C; the crystal size was identified as the main physical property that could explain the CO2 uptake performance of the samples, i.e., the lower the crystal size, the higher the CO2 uptake.

Study on factors in synthesis of lithium orthosilicates powder by solid state reaction method

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Thermodynamic Investigations for Combustion-Assisted Synthesis of Lithium Orthosilicate Powders

Synthesis and Characterization of Inorganic Solid Electrolytes of Li2O-SiO2-P2O5 and Li2O-TiO2-SiO2-P2O5 Systems

Time-Resolved Synchrotron Powder X-ray Diffraction Studies on the Synthesis of Li8SiO6 and Its Reaction with CO2

Understanding the Synthesis of Inorganic Solid-State Electrolytes for Li Ion Batteries: Features and Progress

Optimization of Li4SiO4 synthesis conditions by a solid state method for maximum CO2 capture at high temperature

Synthesis and characterization of single-crystalline phase Li-α-Sialon

The Performance of Li4Ti5O12 and Analysis on the Synthesis Process

Synthesis of Sr1+Xzr4p6-2xsi2xo24 Phosphate Powders by Solid State Reaction

Solid State Synthesis of LiFePO 4 Studied by in Situ High Energy X-ray Diffraction

Synthesis of Li7La3Zr2O12 Solid Electrolyte by Solid Phase Sintering Method

Synthesis and Adsorption Process of Lithium Taking Used as High-Temperature CO2 Sorbents

Synthesis of Bi0.5(Na0.7K0.2Li0.1)0.5TiO3 powders through the molten salt method

Kinetics of novel Li_4SiO_4 absorbing CO_2 at high temperature

Effect of Different Silicon Sources on CO2 Adsorption of Li4SiO4 at High Temperature

Effect of Different Silicon Sources on CO2 Absorption Properties of Li4SiO4 at High Temperature

Enhanced ionic transport in lithium lanthanum titanium oxide solid state electrolyte by introducing silica

Influence of Calcinations Temperature on Crystallization and Synthesis Process of Li<sub>4</sub>Ti<sub>5</sub>O<sub>12</sub>

Synthesis And Characterization Of Single-Crystalline Phase Li-Alpha-Sialon

Preparation of Li 4 SiO 4 from lithium-ion battery cathode waste and diamond wire saw silicon powder using a two-step process