Effect of Thermal Property of Materials on Micro-scale Catalytic Combustion for the Micro Combustor

ZHOU Jun-hu,WANG Yang,YANG Wei-juan,LIU Jian-zhong,WANG Zhi-hua,CEN Ke-fa

DOI: https://doi.org/10.13334/j.0258-8013.pcsee.2010.05.009

2010-01-01

Abstract:Catalyst is applied to enhance the stability of micro combustors effectively.In this experiment,three catalytic micro combustors made of quartz glass,alumina ceramic and copper were tested individually.The catalyst and catalyst support were Pt and asbestus respectively.The combustor was fed with H2/air mixture,and operated under stoichiometric conditions with flow rates from 0.12 to 0.36 L/min.According to the experimental results,catalytic combustors work stably.The temperature distributions on the combustor surface at different operation conditions were measured.Moreover,numeric simulation was applied to investigate the reaction process inside the micro combustor.In the quartz-glass and alumina-ceramic combustor,the temperature distribution shows obvious hot spot.At 0.12 L/min,the peak temperatures are around 1 475 K and 1 427 K,respectively.However,the temperature in the copper combustor is relative lower and distributes uniformly.Its peak temperature does not exceed 1 200 K.According to the comparison of heat loss in different combustors,the combustor with lower thermal conductivity exhibits higher heat loss,which is different from the conventional scale.For example:at the flow rate of 0.12 L/min,the quartz-glass combustor has 2.61 W higher heat loss than the copper combustor.The phenomenon is attributed to the transfer of the reaction mode.In the quartz-glass and alumina-ceramic combustor,homogeneous reaction dominates.But in the copper one,heterogeneous reaction dominates.