Abstract:Moment-resisting steel frames often fail by fracture failure of beam-to-column welded joints during a strong earthquake. This paper provides a numerical methodology based on micromechanics damage model instead of traditional fracture analytical methods to investigate the crack initiation and propagation of welded beam-to-column joints subjected to monotonic loading and ultra low cycle loading conditions. Firstly, parameters used in the micromechanics damage model for steel base metal, heat affected zone and weld metal were calibrated, respectively, against uniaxial tension test results and cycle test results of notched specimens. The evolution of void growth in the notched specimens under different loading conditions was compared. Secondly, fracture process of the welded joints subjected to tensile loading was simulated based on the micromechanics damage model. The predicted load displacement response agrees well with the other researcher's test results. Finally, the micromechanics damage model was applied numerically to investigate the ultra low cycle fatigue fracture behavior of the welded joints under constant amplitude as well as variable amplitude inelastic cyclic loading. According to the distribution and evolution of void in the welded joints obtained from finite element analysis, crack initiation and propagation were presented and the number of cycles to fracture was predicted. It is shown that the fatigue life predicted from finite element analysis based on micromechanics damage model agrees well with the other's test results. (C) 2013 Elsevier Ltd. All rights reserved.

Discussion on Low-cycle Damage Accumulation Assessment Approaches of Steel Beam-to-column Joint Under Seismic Loading

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Low-Cycle Fatigue Damage of Circular Concrete-Filled-Tube Columns

Low-Cycle Fatigue Test of Circular Concrete Filled Tubular Columns

Damage Cumulation Analysis of Welded Joints under Low Cycle Loadings

Low-cycle fatigue test of CFT and CCFT columns

Research on CFRP confined circular concrete-filled steel tubular columns subjected to cyclic lateral forces

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Experimental Study on Reduced I-beam to CFRST Column Joints under Cyclic Loading

Seismic Analysis of Steel Structures Considering Damage Cumulation

Development of a Damage Model for Assessing Fracture Failure of Steel Beam-to-column Connections Subjected to Extremely Low-Cycle Fatigue

Experimental and numerical investigations on extremely-low-cycle fatigue fracture behavior of steel welded joints

Damage Behavior of Steel Beam-to-column Connections under Inelastic Cyclic Loading

Cumulative damage model for steel weld under low-cycle fatigue

On cumulative damage of Q235 steel under low cycle fatigue

Extremely low cycle fatigue prediction of steel beam-to-column connection by using a micro-mechanics based fracture model

Prediction Of Fracture Behavior Of Beam-To-Column Welded Joints Using Micromechanics Damage Model

Investigation on the Weld Damage Behavior of Steel Beam-to-column Connection

Seismic Low-Cycle Fatigue Evaluation of Welded Beam-to-column Connections in Steel Moment Frames Through Global–local Analysis

Damage Evaluation and Ultra-Low-cycle Fatigue Analysis of High-Rise Steel Frame with Mesoscopic Fracture Models