Abstract:The microstructure and hydrogen storage properties of Ti10+x V80-x Fe6Zr4 (x = 0, 5, 10, 15) alloys have been studied. XRD and SEM analyses show that all alloys consist of a BCC main phase and a small fraction of C14 Laves secondary phase, in which the latter precipitates along the grain boundary of the former becoming network structure. With increasing Ti content in the alloy, the lattice parameter and cell volume of the BCC main phase of the alloy increase. The chemical composition of each phase is analysed by EDS, from which the lattice parameters of BCC phase have a good linear relationship with their average atomic radii. All bulk alloys have good activation behaviors and hydriding kinetics. With the increase of Ti content, the incubation time for activation decreases first and then increases under an initial hydrogen pressure of 4 MPa at 298 K. The incubation time of Ti15V75Fe6Zr4 alloy is only 12 s. It is one of the shortest incubation time in V-based solid solution alloys as far as we know, which may be related to the existence of C14 Laves phase. All the alloys have relatively high hydrogen absorption capacities of above 3 wt%, which increase first and then decrease as the Ti content increases, achieving the maximum capacity of 3.61 wt% at x = 10 at 298 K. With increasing x, the equilibrium plateau pressure of dehydrogenation of the samples at 353 K decreases owing to the expansion of unit cell of main phase, which is far below 0.1 MPa for x = 10 and 15. The maximum desorption capacity of 1.94 wt% (desorbed to 0.001 MPa) is obtained at x = 5, compared to that of 1.6 wt% (desorbed to 0.1 MPa) achieved at x = 0.

Hydrogen storage and cyclic properties of V60Ti (21.4+x)Cr(6.6-x)Fe12 (0 ≤ x ≤ 3) alloys

Microstructure and hydrogen storage properties of Ti10+xV80-xFe6Zr4 (x=0~15) alloys

Microstructures and hydrogen storage characteristics of (Ti0.1V0.9)(100-x)Fe-x (x=0 similar to 6) alloys

Development of Ti–Zr–Mn–Cr-(V–Fe) Based Alloys for Hydrogen Feeding System in Hydrogen Metallurgy Application

The Effect of Cr Content on the Structural and Hydrogen Storage Characteristics of Ti10V80−xFe6Zr4Crx (x = 0–14) Alloys

Influence of Fe Content on the Microstructure and Hydrogen Storage Properties of Ti16Zr5Cr22V57−xFex (x = 2–8) Alloys

Hydrogen Storage Properties of Ti-Cr-Mn-M (M=V, Fe, Ni, Cu) Alloys

Hydrogen storage properties of V+TiFe0.85Mn0.15 multi-phase alloys

Phase structures and electrochemical behaviors of V2.1TiNi 0.5Hf0.05Crx (x=0-0.152) hydrogen storage alloys

Hydrogen Storage Properties and Crystal Structure of Ti-Cr Based Alloys

Phase Structures and Hydrogen Storage Properties of TiV1.35Cr1.35-xMnx Alloys(x=0～0.45)

Phase Structure and Hydrogen Storage Properties of Ti17cr23v55-Xzr5fex (X=11 Similar to 16) Alloys

Effect of Fe and Al on hydrogen storage properties of 75 V-Ti-Cr alloys

Microstructures and Hydrogen Storage Properties of Ti10V83-xFe6ZrMnx Alloys

Dependence of Hydrogen Storage Capacity of TiCr1.8−X(VFe)X on V–Fe Content

Hydrogen storage performance of Ti–V-based BCC phase alloys with various Fe content

Microstructure and hydrogen storage properties of Ti10+V80-Fe6Zr4 (x=0~15) alloys

Hydrogen Storage Properties of FeTi1.3 + X Wt%mm (x = 0.0, 1.5, 3.0, 4.5, 6.0) Hydrogen Storage Alloys

Phase structures and hydrogen storage properties

Microstructure and hydrogen storage properties of Ti10V84-xFe6Zrx (x = 1-8) alloys

Effect of dehydrogenation depth on cyclic hydrogen desorption properties of V40Ti25.5Cr26.5Fe8 alloy