Abstract:High Nb-TiAl alloys, which being regarded as a new generation TiAl alloy, had attracted more and more attention for their higher operating temperature and better oxidation resistance than conventional TiAl alloys. It was found that silicide particles in high Nb-TiAl alloys were Nb5Si3 rather than Ti5Si3 precipitated in TiAl alloys. In this work, the effect of Nb5Si3 phase on the microstructure and room-temperature tensile properties of high Nb-TiAl alloy was studied. The experimental results showed that the precipitation temperature of silicide was between 1000 similar to 1200 degrees C. Precipitates located in the colony boundary, beta(B2) segregation and between gamma/alpha(2) lamella. The tensile properties of as-cast alloy with Si addition increased. Because the formation of Nb5Si3 precipitates resulted in the reduction of Nb content, which was one of beta(B2) phase stable elements. Therefore, the volume fraction of beta(B2) phase obviously decreased due to Si addition. However, after heat treatments, the tensile properties of Si containing high Nb-TiAl alloy gradually reduced with the increasing of heat treatment temperature. Silicide particles which precipitated along lamella leaded to generation and propagation of cracks. Moreover, silicide particles further precipitated due to tensile stress which increased the rate of crack propagation. Si addition leaded to gamma phase area expanded. gamma single-phase region formed between 1280 similar to 1300 degrees C. Silicide precipitated in colony boundary resulted in bulk gamma+beta(B2) phases, which weaken the grain boundaries. While suicide precipitated in lamella leaded to formation of secondary gamma lath which split the initial lamella microstructure.

Effect of Si and Ti on Microstructures and Mechanical Properties of Nb-6Hf-4Zr-2B Alloy at Room Temperature

Effects of Ni, Co, B, and Ge on the microstructures and mechanical properties of Nb-Ti-Si ternary alloys

Effects of B Addition on the Microstructure and Properties of Nb Silicide Based Ultrahigh Temperature Alloys

Effect of Ti and Al Interaction on Microstructures and Mechanical Properties of the Nb-Ti-Si-Al Alloys

Effects of Alloying and High-Temperature Heat Treatment on the Microstructure of Nb–Ti–Si Based Ultrahigh Temperature Alloys

Microstructures and mechanical properties of directionally solidified multi-element Nb-Si alloy

Effects Of Ti Content On Microstructure And Phase Compositions Of Nb-Si Based Ultrahigh Temperature Alloy

Effects of B and Si on the Fracture Toughness of the Nb–Si Alloys

Microstructure, mechanical properties and oxidation resistance of Nb silicide based ultrahigh temperature alloys with Hf addition

Microstructural Characteristics of Nb–Si Based Ultrahigh Temperature Alloys with B and Hf Additions

Alloying effects on the microstructure and properties of Nb–Si based ultrahigh temperature alloys

Effect of B and Ti on the Directionally Solidified Microstructure of the Nb–Si Alloys

Microstructural Evolution and Mechanical Behaviour of Nb–10Hf–15W Alloy Doped with Si

Effects of Minor Si on Microstructures and Room Temperature Fracture Toughness of Niobium Solid Solution Alloys

Effect of Si Content on Mechanical Properties of Nb-Si Based Alloys with Nb-Ss/Nb5si3 Structure

Microstructure and Fracture Toughness of Nb-Si Based Alloys by with Ti, Zr and Hf Additions

Effect of Si Addition on the Microstructure and Room Temperature Tensile Properties of High Nb-Tial Alloy

EFFECT OF Si ON MICROSTRUCTURE AND FRACTURE TOUGHNESS OF DIRECTIONALLY SOLIDIFIED Nb SILICIDE ALLOYS

Effect of Ti Addition on Microstructure and Crystalline Orientations of Directionally Solidified Nb–Si Based Alloys

Microstructure, Mechanical Properties and Fracture Behavior of Nb with Minor Si Addition

Collaborative Optimization of Microstructure, Phase Composition and Room-Temperature Fracture Toughness of Nb−Si Based Alloys Using Ti, Zr and Hf Elements