Abstract:Four Nb-Si based ultrahigh temperature alloys with compositions of Nb-22Ti-16Si-3Cr-3Al-xHf (x = 0, 2, 4 and 8, at%) were prepared by vacuum non-consumable arc melting and then they were heat-treated at 1450 degrees C for 50 h. The effects of Hf content on the microstructures of the alloys under both as-cast and heat-treated conditions were investigated. The results show that the microstructure of the as-cast alloy without Hf is mainly comprised of primary alpha(Nb,X)(5)Si-3 blocks, Nbss dendrites and two types of eutectic structures, namely Nbss/alpha(Nb,X)(5)Si-3 and Nbss/gamma(Nb,X)(5)Si-3. The addition of 2 at% Hf causes the formation of primary gamma(Nb,X)(5)Si-3 and increases the content of Nbss/gamma(Nb,X)(5)Si-3 eutectic. With the increasing of Hf content up to 4 at% or 8 at%, the formation of alpha(Nb,X)(5)Si-3 is completely suppressed and the silicide is only present in the form of gamma(Nb,X)(5)Si-3. The Nbss dendrites and typical eutectic structures emerging in the as-cast alloys are almost no longer observable, and the microstructural homogeneity is improved after 1450 degrees C/50 h heat-treatment. The constituent phases of the alloys without Hf or with 2 at% Hf do not change after the heat-treatment. However, the amounts of alpha(Nb,X)(5)Si-3 in the two heat-treated alloys decrease. In addition, the Cr2Nb Laves phase is not found any more in the heat-treated alloys with 4 at% or 8 at% Hf, while a small amount of (Nb,X)(3)Si with a claviform shape is observed in the latter alloy.

Effect of Si Content on Mechanical Properties of Nb-Si Based Alloys with Nb-Ss/Nb5si3 Structure

Microstructural Evolution and Mechanical Behaviour of Nb–10Hf–15W Alloy Doped with Si

Effects of B Addition on the Microstructure and Properties of Nb Silicide Based Ultrahigh Temperature Alloys

Effects of Hf on Mechanical Properties of Nb-15W-5Si-2B Alloy at Room-temperature and High-temperature

Microstructure, mechanical properties and oxidation resistance of Nb silicide based ultrahigh temperature alloys with Hf addition

Effects of B and Si on the Fracture Toughness of the Nb–Si Alloys

Effect of Si and Ti on Microstructures and Mechanical Properties of Nb-6Hf-4Zr-2B Alloy at Room Temperature

Microstructures and mechanical properties of directionally solidified multi-element Nb-Si alloy

Effects Of Ti Content On Microstructure And Phase Compositions Of Nb-Si Based Ultrahigh Temperature Alloy

Effects of Minor Si on Microstructures and Room Temperature Fracture Toughness of Niobium Solid Solution Alloys

Effects of Alloying and High-Temperature Heat Treatment on the Microstructure of Nb–Ti–Si Based Ultrahigh Temperature Alloys

Microstructure, Mechanical Properties and Fracture Behavior of Nb with Minor Si Addition

Effect of Hf on High-Temperature Strength and Room-Temperature Ductility of Nb–15W–0.5Si–2B Alloy

Effect of Ni on Microstructures and Mechanical Properties for Multielemental Nb–Si-Based Alloys

Effect of Ti and Al Interaction on Microstructures and Mechanical Properties of the Nb-Ti-Si-Al Alloys

Nb Content on the Mechanical Alloying Behavior and Sintered Microstructure of Mo-Nb-SiB Alloys

Effects of Alloying on the Microstructures and Mechanical Property of Nb-Mo-Si Based in Situ Composites

Microstructural Characteristics of Nb–Si Based Ultrahigh Temperature Alloys with B and Hf Additions

Alloying effects on the microstructure and properties of Nb–Si based ultrahigh temperature alloys

Microstructure and High-Temperature Mechanical Properties of Nb-Silicide Based In-Situ Composites

Effects of Ni, Co, B, and Ge on the microstructures and mechanical properties of Nb-Ti-Si ternary alloys