Abstract:Well-aligned small-diameter ZnO nanowire arrays have been synthesized on Si wafers pre-coated with c-oriented ZnO thin films by a catalyst-free thermal evaporation method. The morphology of the products has been found to be greatly affected by the oxygen flow rate. The self-catalyzed VLS mechanism is proposed to interpret the growth of the ZnO nanowires and the change in the product morphology. Classical nucleation theory is employed to analyze the growth process of the ZnO nanowires, and Zn vapor supersaturation is proposed to be a key factor to affect the diameter and the areal density of the ZnO nanowires. The average diameter of the ZnO nanowires can be finely controlled in the range of 12-31 nm by controlling the oxygen flow rate and hence the Zn vapor supersaturation. This result is consistent with our theoretical prediction. X-ray photoelectron spectroscopy measurements were performed to characterize the stoichiometry of nanowires with various average diameters. It also revealed that there are many OH species on the nanowire surface. Photoluminescence measurements showed that the deep-level emission of the nanowires with average diameter of 12 nm peaks in the yellow region, which may be attributed to the presence of OH species and surface effects.

A catalyzed-growth route to directly form micropatterned WO2 and WO3 nanowire arrays with excellent field emission behaviors at low temperature

Ultrafast growth of single-crystalline Si nanowires

A Low-Temperature Method to Selected-Area Synthesis of Tungsten Oxide Nanowire Arrays and Investigation on Their Field Emission Properties

P1–8: Low Temperature Gowth and Field Emission Properties of Patterned Tungsten Oxide Nanowire Arrays by Using Cceramic Template

P1-8: Low temperature gowth and field emission properties of patterned tungsten oxide nanowire arrays by using cceramic template

A novel lift-off method for fabricating patterned and vertically-aligned W18O49 nanowire arrays with good field emission performance.

Fabrication of patterned aligned W18O49 nanowire arrays with high field emission performances

A simple SVS method for obtaining large-scale WO3 nanowire cold cathode emitters at atmospheric pressure and low temperature

A Simple SVS Way to Obtain Large-scale WO3 Nanowire Cold Cathode Emitters at Atmospheric Pressure and Low Temperature

Field-Emission Properties of Nanostructured Wo3 Arrays Fabricated Using Tungsten Hot-Filament Chemical Vapor Deposition

A facile solution route to deposit TiO2 nanowire arrays on arbitrary substrates.

High FE current density from tungsten oxide nanowires

Controlled synthesis of patterned W18O49 nanowire vertical-arrays and improved field emission performance by in situ plasma treatment

Template Deformation‐Tailored ZnO Nanorod/Nanowire Arrays: Full Growth Control and Optimization of Field‐Emission

Growth mechanism and diameter control of well-aligned small-diameter ZnO nanowire arrays synthesized by a catalyst-free thermal evaporation method.

Controlled Preparation of Micron-Size-Pattemed ZnO Nanowire Field Emitters

A novel synthesis method of large-area tungsten oxide nanowires arrays and their field emission properties

Controlled Growth of Large-Area, Uniform, Vertically Aligned Arrays of α-Fe<sub>2</sub>O<sub>3</sub>Nanobelts and Nanowires

Large-Area Nanowire Arrays of Molybdenum and Molybdenum Oxides: Synthesis and Field Emission Properties

A New Method for Bulk-Quantity Synthesis of Patterned Well-Aligned Zno Nanowire Arrays

Growth of Large-Area Aligned Molybdenum Nanowires by High Temperature Chemical Vapor Deposition: Synthesis, Growth Mechanism, and Device Application