In Situ ESR and TPSR Measurements of SrTi0.975Li0.025O3-δ Nanocatalysts for Oxidative Coupling of Methane at Low Temperature

宋国华,缪建文,范以宁,周静

DOI: https://doi.org/10.3969/j.issn.0253-2409.2010.04.019

2010-01-01

Abstract:Perovskite-type SrTi1-xLixO3-δ(x = 0,0.025,0.050) nano catalyst was prepared by using sol-gel method.Its structure was characterized by X-ray diffraction(XRD),transmission electron microscopy(TEM),in-situ electron spin resonance(ESR),and temperature-programmed surface reaction(TPRS);its catalytic performance for oxidative coupling of methane(OCM) was measured in a microreactor.The results indicated that the OCM catalytic performance at low temperature(about 650 ℃) is enhanced by doping Li+ cation to the B site of perovskite-type SrTiO3 nano catalysts;the SrTi1-xLixO3-δ nano catalyst with x = 0.025 performs best.Compare with the conventional catalysts of the same composition prepared by citric acid method,SrTi0.975Li0.025O3-δ nano catalyst performs much better for OCM reaction at low temperature;higher C2 selectivity is achieved at the same temperature.In-situ ESR results showed that there exist O-with ESR signal at g = 2.043 0 and F center with ESR signal at g = 2.008 0 in the nano SrTi0.975Li0.025O3-δ catalyst,while the conventional SrTi0.975Li0.025O3-δ catalyst shows O2-with the ESR signals at g∥ = 2.014 and g⊥ = 1.990 6.The high catalytic performance of SrTi0.975Li0.025O3-δ nano catalyst is related to F centers due to the low coordination surface atoms on the nano oxide particles.F center may activate CH4 at lower temperature and lead to the formation of C2 hydrocarbons with higher selectivity.