Abstract:New Cu-based bulk glassy alloys were formed in Cu–Zr–Ti and Cu–Hf–Ti systems by the copper mold casting method. The critical diameter is 4 mm for the Cu60Zr30Ti10 and Cu60Hf25Ti15 alloys which are larger than 1 mm for the Cu60Zr40 and Cu60Hf40 glassy alloys. The substitution of Zr or Hf for Ti causes an increase in the glass-forming ability (GFA). As the Ti content increases, the glass transition temperature (Tg), crystallization temperature (Tx), and the supercooled liquid region ΔTx(=Tx−Tg) decrease for both Cu60Zr40−xTix and Cu60Hf40−xTix alloys. In contrast, the liquid temperature (Tl) has a minimum value of 1127 K for the Cu60Zr20Ti20 alloy and 1175 K for the Cu60Hf20Ti20 alloy, resulting in a maximum Tg/Tl of 0.63 and 0.62, respectively. The alloys with the highest Tg/Tl value showed the highest GFA for these Cu-based alloys. The bulk glassy alloys exhibit high tensile fracture strength of 2000–2160 MPa, compressive fracture strength of 2060–2150 MPa and compressive plastic elongations of 0.8–1.7%. The finding of the new Cu-based bulk glassy alloys with high GFA, high fracture strength above 2000 MPa and distinct plastic elongation is encouraging for the future development of a new type of bulk glassy alloy which can be used for structural materials.

New type of Zr-Al-Ni-Cu bulk metallic glass with high plasticity at room temperature

A Plastic Zr–Cu–Ag–Al Bulk Metallic Glass

Enhanced Plasticity in a Zr-based Bulk Metallic Glass Containing Nanocrystalline Precipitates

Formation, Thermal Stability and Mechanical Properties of Zr-Nb-Cu-Ni-Al Bulk Metallic Glasses

Formation and mechanical properties of bulk Cu-Ti-Zr-Ni metallic glasses with high glass forming ability

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

A Novel Ni-Free Zr-Based Bulk Metallic Glass with High Glass Forming Ability, Corrosion Resistance and Thermal Stability

New Class of Plastic Bulk Metallic Glass.

High-strength Cu-based bulk glassy alloys in Cu–Zr–Ti and Cu–Hf–Ti ternary systems

Homogeneity of the Superplastic Zr64.13Cu15.75Ni10.12Al10 Bulk Metallic Glass

Cu-Based Bulk Glassy Alloys with Good Mechanical Properties in Cu-Zr-Hf-Ti System

Ni-free Zr-based bulk metallic glasses with critical diameter above 20mm

Cu-based bulk glassy alloys with high tensile strength of over 2000 MPa

Plasticity-improved Zr–Cu–Al Bulk Metallic Glass Matrix Composites Containing Martensite Phase

Composition design and mechanical properties of ternary Cu–Zr–Ti bulk metallic glasses

Mechanical Properties of Monolithic Zr62Al8Ni13Cu17 Bulk Metallic Glass

Enhancement of Plasticity in Zr-based Bulk Metallic Glasses

Structure and properties of Zr–Ta–Cu–Ni–Al bulk metallic glasses and metallic glass matrix composites

A Ti-based bulk glassy alloy with high strength and good glass forming ability

Superductile Bulk Metallic Glass

Synthesis of Centimeter-Size Ag-doped Zr–Cu–Al Metallic Glasses with Large Plasticity