Abstract:5005 aluminum alloy and hot-dip aluminum stainless steel were brazed using Al-Si-Mg solder. The interfacial structure and its effect on shear strength of the joints were studied in this paper. The results show that the best processing parameters are 600°C, 15 min and the interfacial structures are stainless steel/FeAl/FeAl3/FemAln+Mg2Si+αAl/5005 aluminum alloy. With the increasing brazing temperature or the extending holding time, the shear strength of joints increases and then decreases. The maximum shear strength can reach 33 MPa. Fracture tests show that the form of fracture is brittle fracture and fracture usually occurs in the solder seam.

Study on the interface microstructure and mechanical properties of 5005 aluminum alloy and stainless steel brazed joint