Abstract:The Mg-Al series alloys are well known for their low density, high specific strength, and superior damping capability. However, the application of Mg-Al series alloys is often limited by inadequate mechanical properties. To fulfill the growing demand for lightweight structural components, ultrafine grained magnesium alloys with superior mechanical properties have gained attention. Mechanical milling and powder metallurgy were used to produce the AZ61 ultra-fine grained magnesium alloy with super-high tensile characteristics. The effects of mechanical milling on the grain size, precipitates, texture, and tensile properties of AZ61 ultra-fine grained magnesium alloy were investigated. The grain size of the AZ61 alloy produced by mechanical milling and powder metallurgy was reduced from 0.91 mu m to 0.68 mu m when compared to that produced by non-mechanical milling. Mechanical milling accelerated the dynamic precipitation and refining of Mg 17Al 12 while weakening the basal texture. The yield strength, tensile strength, and elongation of AZ61 ultra-fine grained magnesium alloy are 393.1 MPa, 431.9 MPa, and 8.5%, respectively, which are superior to the AZ61 alloy produced by other processes. The theoretical grain refinement and Orowan strengthening mechanisms of AZ61 alloy were calculated, and it shows that the grain refinement strengthening contributes more than 90% of the yield strength. The Orowan strengthening was overestimated when Mg 17Al 12 was distributed at grain boundaries. The weakening of basal texture resulted in a reduction in yield strength. The fracture mechanism of the AZ61 alloy without mechanical milling is dominated by oxidation on the surface of the AZ61 powder, which initiates interparticle debonding. The fracture mechanism of the AZ61 alloy with mechanical milling is dominated by deformation mismatch between the deboned powders and the stronger bonded powders, and the increase in the amount of Mg 17Al 12 along the grain boundary.

Microstructures and Mechanical Properties of High Strength AZ91 Mg Alloy by Spray Forming Technology

Effect of Si on Microstructure of Spray Formed AZ91 Mg Alloy

Microstructure and Mechanical Properties of 7055 Al Alloys by Spray Forming

Study of the microstructure, texture and tensile properties of as-extruded AZ91 magnesium alloy

Microstructure and Tensile Properties of AZ61 Alloy Sheets Processed by High-Ratio Extrusion with Subsequent Direct Aging Treatment

Microstructures and tensile properties of spray-deposited high-strength aluminium alloys

Characterization of Hot Extrusion and Heat Treatment on Mechanical Properties in a Spray Formed Ultra-High Strength Al-Zn-Mg-Cu Alloy

Mechanical Properties and Microstructures of Mg-Al-Zn Alloys with High Aluminum Contents

Study on Microstructure and Mechanical Properties of A356 Aluminum Alloy by Spray Forming

Microstructures and Mechanical Properties Ofaz91d Magnesium Alloy Processed by Low Pressure Die Casting

Microstructure and Properties of AZ61 Ultra-Fine Grained Magnesium Alloy Prepared by Mechanical Milling and Powder Metallurgy Processing

Achieving High Performance by Optimized Heat Treatment in a Spray Formed Al–Zn–Mg–Cu Alloy

INFLUENCE OF SOLUTION AND AGING ON MECHANICAL PROPERTIES OF AZ91HP DIE-CASTING ALLOY

Analysis of Section Extrusion and Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

Microstructure Evolution and Mechanical Properties of AZ80 Mg Alloy during Annular Channel Angular Extrusion Process and Heat Treatment

Refined microstructure and improved mechanical properties of high-ratio extruded AZ91−xSn magnesium alloy

Effect of heat treatment and extrusion processing on the microstructure and mechanical properties of spray formed 7055 alloy

Effect of Hot Deformation and Heat Treatment on the Microstructure and Properties of Spray-Formed Al-Zn-Mg-Cu Alloys

Microstructural Evolution through Uniaxial Hot Pressing before Age Hardening of AZ91D Alloy

Surface Grain Refinement of AZ91D Magnesium Alloy by Cold Spraying Shot Peening Process

Study on Microstructure and Mechanical Properties of AZ91D Magnesium Alloy Fabricated by Hot Extrusion from Die-casting Scraps