Effect of Heat Treatment on Tensile Properties, Impact Toughness and Plane Strain Fracture Toughness of Sand-Cast Mg-6Gd-3Y-0.5Zr Magnesium Alloy
Quan Wang,Lv Xiao,Wencai Liu,Haohao Zhang,Wendong Cui,Zhongquan Li,Guohua Wu
DOI: https://doi.org/10.1016/j.msea.2017.08.100
2017-01-01
Abstract:The tensile properties, impact toughness and plane-strain fracture toughness of sand-cast Mg-6Gd-3Y-0.5Zr magnesium alloy were studied in different thermal conditions, including as-cast, as-quenched and isothermal aging states. The results show that optimum heat treatment is solutionized at 490℃ for 12h, and then aged at 212℃ for 100h. Tensile test exhibits that as-quenched GW63 alloy shows high elongation but low tensile strength, nevertheless, aged alloy shows higher strength but worse ductility. Impact values of GW63 alloy are 34.6, 50.9 and 20.3J/cm2 in the as-cast, as-quenched and aged states, respectively. Room temperature impact toughness is more closely related to material ductility than strength for the studied alloy. The plane-strain fracture toughness values of the as-cast, as-quenched and aged alloy are 16.2, 17.7 and 19.5MPam½, respectively, i.e., the improvement of 20.4% has been achieved by aging precipitation strengthening in contrast with slight improvement of 9.3% by solid solution strengthening. In addition, fractured characteristics after impact and fracture toughness tests were also investigated by fracture analysis.