Doping and Grain Size Effects in Nanocrystalline ZrO2–Sc2O3system with Complex Phase Transitions: XRD and Raman Studies
G Xu,YW Zhang,CS Liao,CH Yan
DOI: https://doi.org/10.1039/b413701a
IF: 3.3
2004-01-01
Physical Chemistry Chemical Physics
Abstract:Weakly-agglomerated nanocrystalline (ZrO2)(1-x)(Sc2O3)(x) ( x = 0.02 - 0.16) powders with high surface area (106 - 186 m(2) g(-1)) and uniform particle size (5.7 - 9.5 nm) were synthesized by a two-step hydrothermal process in the presence of urea, and their complex phase evolution upon calcinations over 400 - 1400 degreesC were studied by a combined utilization of X-ray diffraction, in situ high temperature X-ray diffraction, near infrared Fourier transform Raman and ultraviolet Raman spectroscopies. It was discovered that the growth of the grains comprised two stages, and the apparent activation energies, E-a1 (<800 degrees C) and E-a2 (>800 degreesC), are in the range of 5.5 - 12 kJ mol(-1) and 80 - 140 kJ mol(-1), respectively. The crystallite size, microstrain, surface area and growth activation energy of the samples showed a strong dependence on the Sc3+ doping concentration. The nanocrystalline (ZrO2)(1-x)(Sc2O3)(x) samples underwent complex phase transitions upon calcination from 800 to 1000 degreesC. Tetragonal and cubic phases have been preserved when the samples calcined below 800 degreesC as a result of crystallite size and doping effects. At elevated calcination temperature of 1000 degreesC, the compositions at x = 0.04, 0.10 and 0.14 seemed to be in the metastable phase boundaries of m + t, t + beta (Sc2Zr7O17) and beta+gamma (Sc2Zr5O13), respectively. As calcined at 1400 degreesC, the grain size was in the micrometre regime, and t --> m, c --> t", c --> beta and c --> gamma phase transitions occurred on the cooling stage for x less than or equal to 0.04, x = 0.08, 0.10 less than or equal to x less than or equal to 0.12 and x greater than or equal to 0.14, respectively, resulting in the existence of m, t, t", beta and gamma phases in turn at room temperature. Moreover, it was found that the tetragonal phase has been enriched at the surface region for the as-calcined (ZrO2)(0.94)(Sc2O3)(0.06) and (ZrO2)(0.92)(Sc2O3)(0.08) samples.