Abstract:Weakly-agglomerated nanocrystalline (ZrO2)(1-x)(Sc2O3)(x) ( x = 0.02 - 0.16) powders with high surface area (106 - 186 m(2) g(-1)) and uniform particle size (5.7 - 9.5 nm) were synthesized by a two-step hydrothermal process in the presence of urea, and their complex phase evolution upon calcinations over 400 - 1400 degreesC were studied by a combined utilization of X-ray diffraction, in situ high temperature X-ray diffraction, near infrared Fourier transform Raman and ultraviolet Raman spectroscopies. It was discovered that the growth of the grains comprised two stages, and the apparent activation energies, E-a1 (<800 degrees C) and E-a2 (>800 degreesC), are in the range of 5.5 - 12 kJ mol(-1) and 80 - 140 kJ mol(-1), respectively. The crystallite size, microstrain, surface area and growth activation energy of the samples showed a strong dependence on the Sc3+ doping concentration. The nanocrystalline (ZrO2)(1-x)(Sc2O3)(x) samples underwent complex phase transitions upon calcination from 800 to 1000 degreesC. Tetragonal and cubic phases have been preserved when the samples calcined below 800 degreesC as a result of crystallite size and doping effects. At elevated calcination temperature of 1000 degreesC, the compositions at x = 0.04, 0.10 and 0.14 seemed to be in the metastable phase boundaries of m + t, t + beta (Sc2Zr7O17) and beta+gamma (Sc2Zr5O13), respectively. As calcined at 1400 degreesC, the grain size was in the micrometre regime, and t --> m, c --> t", c --> beta and c --> gamma phase transitions occurred on the cooling stage for x less than or equal to 0.04, x = 0.08, 0.10 less than or equal to x less than or equal to 0.12 and x greater than or equal to 0.14, respectively, resulting in the existence of m, t, t", beta and gamma phases in turn at room temperature. Moreover, it was found that the tetragonal phase has been enriched at the surface region for the as-calcined (ZrO2)(0.94)(Sc2O3)(0.06) and (ZrO2)(0.92)(Sc2O3)(0.08) samples.

Phase transition of nanostructure zirconias doped with rare earth elements.

Tetragonal‐to‐Monoclinic Phase Transitions in Nanocrystalline Rare‐Earth‐Stabilized Zirconia Prepared by a Mild Hydrothermal Method

Hydrothermal Synthesis and Characterization of Zirconia Nanocrystallites

Unusual Calcination Temperature Dependent Tetragonal–monoclinic Transitions in Rare Earth-Doped Zirconia Nanocrystals

Crystal Structure of Zirconia by Rietveld Refinement

Influence of Y2O3 Doping on Phase Evolution and Dielectric Characteristics of ZrO2 Ceramics

Phase Composition Controllable Preparation of Zirconia Nanocrystals Via Solvothermal Method

Preparation, crystal structure and electrorheological performance of nano-sized particle materials containing ZrO2

Study of Synthesis and Photocatalytic Performance of the Monoclinic/cubic Heterophase Junction of Rare Earth Doped Zirconia

Optimization of the structure and morphology of monoclinic phase nanoscale zirconium dioxide

Microstructures and Optical Properties of Nanocrystalline Rare Earth Stabilized Zirconia Thin Films Deposited by a Simple Sol–gel Method

Hydrothermal Synthesis of Nanocrystalline ZrO2-8Y2O3-xLn2O3 Powders (Ln = La, Gd, Nd, Sm): Crystalline Structure, Thermal and Dielectric Properties

Synthesis, microstructure and optical characterization of zirconium oxide nanostructures

Li+ co-doping induced phase transition as an efficient strategy to enhance upconversion of La2Zr2O7:Er,Yb nanoparticles

Improving the Mechanical Properties and Microstructure of 12 mol% Ceria-Stabilized Tetragonal Zirconia Polycrystal Ceramics with Low-Content Nd2O3

An EXAFS Study of the Nanocrystalline Transformation of ZrO2:Y2O3(5%)

Effect of zirconium non-stoichiometry on phase structure and electrical properties of (K,Na)(Nb,Sb)O3-(Bi,Na)ZrO3 ceramics

Doping and Grain Size Effects in Nanocrystalline ZrO2–Sc2O3system with Complex Phase Transitions: XRD and Raman Studies

Nanocrystalline Rare Earth Stabilized Zirconia: Solvothermal Synthesis Via Heterogeneous Nucleation-Growth Mechanism, and Electrical Properties

Influence of Crystal Inducing Agent on the Phase Structure and Optical Properties of Nano Zirconia

Cubic phase stability, optical and magnetic properties of Cu-stabilized zirconia nanocrystals