Iron Oxide Based High Temperature Desulfurization Sorbent

Ju Shangguan,Pengfei Hou,Yongjun Zhu,Litong Liang,Fang Shen,Huiling Fan,Maoqian Miao
DOI: https://doi.org/10.1109/ICBBE.2009.5162987
2009-01-01
Abstract:Iron oxide sorbent is used as high temperature desulfurization sorbent due to high sulfur capacity, easy regeneration and recovery elemental sulfur. In this paper, the iron oxide based high-temperature sorbent was obtained by mixing iron oxide with calcium oxide, extrudating and calcinating. The sulfidation, reduction and regeneration performance for the prepared iron oxide based desulfurization sorbent were conducted. The phases of fresh iron oxide based sorbents, sulfided sorbent and regenerated sorbent were characterized by XRD and SEM. There are three reduced peaks corresponding Fe3O4, FeO and Fe for iron oxide based sorbent in temperature-programmed reduction. The breakthrough curve of iron oxide based sorbent in present of H2 and H2S at 500degC and 3600 h-1 shows that outlet concentration of H2S exhibits a peak at early stage, and then approaches a stable until breakthrough. This phenomenon shows that Fe2O3-H2 reaction rate is more rapidly than Fe2O3-H2S reaction. The Fe2O3 reacts rapidly with H2 to form FeO and FeO reacts with H2S to form FeS. This work examined the sulfur compound concentration change during regeneration as a function of temperature. The regeneration reaction is given by 2FeS + 7/2O2 = Fe2O3 + 2SO2 when O2 take as the only reactive component in the feed gas, 3FeS + 4H2O = Fe3O4 +3H2S +H2 when H2O take as the only reactive component in the feed gas. The regeneration rate in O2 is more rapid than that in H2O, and there are big pore on the surface of the regeneration sorbent in oxygen agent compared with the regeneration sorbent in steam agent.
What problem does this paper attempt to address?