Abstract:With the rapid development of the semiconductor industry, the feature size of integrated circuits (ICs) is continuously getting smaller and smaller. Although traditional optical lithography and extreme ultraviolet (EUV) lithography can fabricate products with 5-nm feature size, the production cost is quite high. As a candidate of next-generation lithography, ultraviolet nanoimprint lithography (UV-NIL) can also achieve high-resolution imprints at a lower cost. Based on contact mechanics, the filling mechanism and imprint quality of UV-NIL were examined using high-resolution stamps with different feature sizes of 3 nm, 4 nm, and 5 nm. It was found that UV-NIL could successfully replicate patterns with feature sizes down to 3 nm; however, the imprinting process was more complicated. Among the selected nine stamps, the replications of 4-nm and 5-nm feature sizes had a relatively uniform residual layer and a symmetric contact pressure, whereas the replications of 3-nm feature size had an asymmetric contact pressure, resulting in an asymmetric residual layer. In order to obtain a more uniform residual layer with higher-quality imprinting, the pressure applied to the left and right sides of a stamp should be appropriately changed. The pattern density of a stamp had a certain influence on the contact pressure. As the pattern density increased, the contact pressure tended to be uniform; however, when the pattern density exceeded 0.5, the situation became worse. This research can provide guidance for promoting the development of UV-NIL in the direction of high-resolution pattern replication.

Nanoimprint lithography for complex 3D micro-nano structures replication under low temperature

Focused ion beam–based nanoimprint stamp for replicating micro/nanostructures under low temperature

Research on Micro/nanopattern Fabrication Based on Nanoimprint Lithography at Low Temperature

Optimization and experimentation of nanoimprint lithography based on FIB fabricated stamp

Development of Novel SU-8 Based Nanoimprint Lithography

Three-Dimensional in Situ Electron-Beam Lithography Using Water Ice.

Scalable Lithography From Natural Dna Patterns Via Polyacrylamide Gel

Large area nanosize array stamp for UV-based nanoimprint lithography fabricated by size reduction process

Novel method to mass-produce PDMS stamps based on nanoimprint

Fabrication of Large-Area Nanostructures Using Cross-Nanoimprint Strategy

Application of Lift-Off Process in Fabricating Nanoimprint Stamp

Research on the Filling Process of Ultraviolet Nanoimprint Lithography with High-Resolution Stamps

Nanoimprint lithography technology

Nanostructures and Nanodevices Special Fabrication and Characterization

Applications Of Nanoimprint Lithography For Biochemical And Nanophotonic Structures Using Su-8

High fidelity 3D thermal nanoimprint with UV curable polydimethyl siloxane stamps

DNA Nanostructures-Mediated Molecular Imprinting Lithography.

Duplication of Nanoimprint Templates by a Novel SU-8/SiO2/PMMA Trilayer Technique

Scanning probe lithography for nanoimprinting mould fabrication

A novel method to fabricate complex three-dimensional microstructures

Anti-sticking Treatment for a Nanoimprint Stamp