Abstract:High-temperature superconducting materials (HTS) are characterized by remarkably high critical current density ( J c ) values when exposed to low temperatures and magnetic fields. In the realm of such investigations, various crystalline imperfections, including finely dispersed non-superconducting phases, dislocations, vacancies, grain boundaries, twin boundaries, antiphase boundaries, and insulating regions within grain boundaries, have been recognized as potential sources of pinning centers. However, it is essential to acknowledge that J c values experience a rapid decline as the temperature rises in the presence of a magnetic field. The primary contributing factors to this decline are attributed to the intrinsic crystalline anisotropy of HTS materials and the thermal fluctuations that prevail at elevated temperatures. Nevertheless, a noteworthy factor in the diminishment of J c values is the scarcity of efficacious pinning centers. In response to these challenges, a pioneering technology has emerged, revolving around nanostructure engineering for the deliberate creation of artificial pinning centers within HTS materials. In alignment with this approach, the present study endeavors to augment the critical current density and enhance the flux pinning properties of YBa 2 Cu 3 O 6.56 (YBCO) superconducting films. This augmentation is achieved through the integration of BaIrO 3 (BIO) perovskite nanodots, nanorods, or nanoparticles as strategically positioned pinning centers. The films are deposited on a SrTiO 3 (STO) substrate employing the Trifluoroacetate Metal–Organic Deposition (TFA-MOD) technique. This research initiative seeks to contribute to the advancement of knowledge regarding the controlled manipulation of artificial pinning centers in HTS materials, particularly focusing on YBCO thin films, with the ultimate goal of enhancing their performance under the influence of elevated magnetic fields.

The study of a rotating method for fabricating Y1Ba2Cu3O7-x films by TFA-MOD

The Influence of Gas Flow Rate on the Growth of YBCO Films Prepared by TFA-MOD

Study on the growth rate of YBCO films prepared by TFA-MOD

Artificial Control for Nucleation and Growth Rate of YBa2Cu3O7-δ Coated Conductors Prepared by Low Fluorine Chemical Solution Deposition

In-Plane and Out-of-Plane Anisotropy in the Optical and Dielectric Properties of Yba2cu3o7-X Superconducting Film

Mod-derived YBa2Cu3O7-δ thin filmsusing a fast pyrolysis process

Study on PEG Assisted TFA-MOD Method for Rapid Fabrication of YBa2Cu3O7−δ Thin Films: Influence of PEG Additive Amount in Precursor Solutions

MOD-Derived YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> Thin Films using a Fast Pyrolysis Process

Preparation of Yba2cu3o7-X Superconducting Thin-Films over Large Area Substrates

Thermodynamics and Kinetics Analysis of Mod-Ybco Heat Treatment Process Using in Situ Resistance Measurement Method

Study on the oxygenation process during the heat treatment of TFA-MOD YBCO thin films by in situ resistance measurement

Preparation of YBa2Cu3O7−δ Films by MOD Method Using Trifluoroacetate As Precursor

Synthesis and characterization of BaIrO3-doped YBCO superconducting thin films via TFA-MOD technique

Formation and Characterization of YBa2Cu3O7−δ High-Tc Thin Films by MOCVD with Single Mixed Precursor

Low-Vacuum Pyrolysis of YBCO Films by Using Fluorine-Free Metal Organic Chemical Deposition

Influence of Partial Melting Temperature on Structure and Superconducting Properties of YBCO Film by Non-fluorine MOD

Precursor evolution and growth mechanism of BTO/YBCO films by TFA—MOD process

STUDY OF THE PREPARATION OF HIGH Tc SUPERCONDUCTING YBCO THIN FILMS BY A PLASMA-ASSISTED MOCVD PROCESS

A Low-Fluorine Solution With A 2:1 F/Ba Mole Ratio For The Fabrication Of Ybco Films

Property Improvement of 600-Nm-thick YBCO Superconducting Films Fabricated Using a Pb-Modified MOD Method

Research of YBa2Cu3O7-δPyrolysis Films with Different Surface Morphologies by Low-Fluorine Metallorganic Deposition