Excitation Wavelength Dependence Of The Visible Photoluminescence From Amorphous Zno Granular Films

Wei Zhang,Xinglong Wu,Haitao Chen,Jinsong Zhu,Guo Huang
DOI: https://doi.org/10.1063/1.2924421
IF: 2.877
2008-01-01
Journal of Applied Physics
Abstract:Amorphous ZnO granular films were fabricated by anodizing zinc sheet in 0.5M oxalic acid solution under direct current voltage. The photoluminescence spectrum of the as-anodized sample shows a very broad visible emission band, which can be Gaussian divided into two subbands at 525 and 600 nm. Based on their annealing behavior and the growing mechanism of the ZnO films, the two subbands are attributed to optical transitions in oxygen vacancies and oxygen interstitials, respectively. Obvious redshifts of the two subbands were observed with increasing excitation wavelength. Spectral analyses suggest that the excitation wavelength dependences of the two subbands are due to the quantum confinement on the amorphous ZnO nanoparticles mainly with sizes of similar to 10 nm. This work provides a good understanding of the photoluminescence behavior of amorphous ZnO particles. (c) 2008 American Institute of Physics.
What problem does this paper attempt to address?