Abstract:In this paper, mechanical properties and microstructures of the cast and extruded Al-xCu-1Li-0.4Mg–1Zn-0.1Zr alloys (x = 2.0, 3.0, 4.0, 4.5, 5.5, 6.5 wt%) were investigated. The results showed that the as-cast micrographs of alloys with different Cu content primarily consist of dendritic α-Al grains, and the intermetallic phases at the grain boundaries were Cu and Zr rich phases. After solution treatment, no recrystallization took place in extruded alloys, and the alloys mainly represented mixed textures composed of <111> and <100> fibers. Cu significantly affected the precipitation behavior of the extruded alloys. Only T1 (Al2CuLi) phases were observed in T6 (aging at 175 °C for 32 h) and T8 (3% pre-strain followed by aging at 150 °C for 32 h) treated alloy with 2 wt% Cu. Further increasing Cu contents (4.5 and 6.5 wt%) enabled the co-precipitation of T1 and θ' (Al2Cu) phases, as well as increased their density. In addition, the microstructures of grain boundaries of alloys with different Cu content showed dramatic differences. T1 phases precipitated at the grain boundaries of alloy containing 2 wt% Cu, while rare precipitation of T1 phases was observed at the grain boundaries of alloy with 6.5 wt% Cu. The yield strength (YS) of the alloys increased with the Cu content and the elongation (EL) showed an opposite trend. A good combination of ultra-high strength (YS = 684 MPa, ultimate tensile strength = 726 MPa) and ductility (EL = 6.3%) was obtained in T8 treated alloy containing 4.5 wt% Cu. The presence of the undesired coarse T2 (Al6CuLi3) phases at the grain boundaries resulted in the premature failure of the high Cu content alloys.

Graded Distribution of Microstructure in Centrifugal-Cast Al-CU Alloys

Evolution jof microstructure in centrifugal cast Al-Cu alloy

Research of Mechanical Property Gradient Distribution of Al-Cu Alloy in Centrifugal Casting

Study on shrinkage cavity in centrifugal cast Al-Cu alloys

Experimental and numerical studies on the influence of centrifugal casting parameters on the solidification structure of Al-Cu alloy

Coupling Simulation and Mechanism Analysis of Grain Formation and Growth in Horizontal Centrifugal Casting

Numerical Simulation of Microstructure Evolution of Ti-6al-4v Alloy in Vertical Centrifugal Casting

Influence of Super Gravity Field on Solidification Structures of Cu98.4 Cr1.6 Alloy

Investigation on microstructure heterogeneity of the HPDC AlSiMgMnCu alloy through 3D electron microscopy

Microstructure Formation in Centrifugally Cast Al–Bi Alloys

Evolution of Solidification Microstructure of Centrifugal Cast Ti–6Al–4V Alloy

Transient Modeling Of Grain Structure And Macrosegregation During Direct Chill Casting Of Al-Cu Alloy

Relationship Between Microstructures and Mechanical Properties of Ti-6Al-4V Alloy in Centrifugal Casting

Study on Microstructure Distribution of Al-Cu-Mg Alloy in Squeeze Casting Process

Characterization of a functionally graded directionally solidified Al-33Cu alloy

Evolution of the Second-Phase Particles and Their Effect on Tensile Fracture Behavior of 2219 Al-xCu Alloys

Microstructural evolution and mechanical properties of cast Al‐2.6Li‐2.8Mg‐(0.5, 1.4)Cu‐0.2Zr‐0.2Sc alloys during heat treatment

Effect of Solution Treatment on Microstructures and Mechanical Properties of Centrifugal Casting Al-Cu Alloy

Microstructural Characterization of the As-Cast and Homogenized Al-Cu-Mg-Ag Alloy

Role of Cu on the Mechanical Properties and Microstructures Evolution of Al-xCu-1Li-0.4Mg–1Zn-0.1Zr Alloys

Microstructure Evolution and Mechanical Properties of a Cast and Heat-Treated Al–Li–Cu–Mg Alloy: Effect of Cooling Rate During Casting