Abstract:Capacity and voltage fading of lithium-and-manganese-rich (LMR) cathodes is a major challenge for the application of this category of material, which is believed to be associated with the structural and chemical evolution of the materials.[1-3] As one of the most promising cathode materials for next generation lithium ion batteries, LMR cathode materials have the expression xLiMO2·(1-x)[Li2MnO3] (M=Mn, Ni, Co, 0≤x<1). As the parent component of LMR, Li2MnO3 cathode materials also attracted much attention for many reasons. First, Li2MnO3 itself has a very high theoretical capacity. Second, it can enhance our fundamental understanding of the electrochemistry of Mn-containing cathode materials. Thirdly, we can obtain the knowledge necessary for design new LMR cathode materials. Li2MnO3 cathode was initially believed electrochemical inert because all the Mn cations are Mn in this material until Kalyani et al. demonstrated that Li2MnO3 could be electrochemically activated in 1999.[4] It has been claimed that prolonged cycling could transform Li2MnO3 to LiMn2O4-spinel.[5, 6] However, recently X-ray absorption spectroscopy results from cycled sample are not consistent with the LiMn2O4-spinel structure, instead the P3 structure was proposed.[7] In a chemically delithiated Li2MnO3 sample, Wang et al. observed the formation of MnO2 phase.[8] Up to now, it is still not clear which structure is formed after charge-discharge cycles and how the structure evolves during the cycling of Li2MnO3 cathode. In this work, we report the detailed structural and chemical evolutions of Li2MnO3 cathode captured by using aberration corrected scanning/transmission electron microscope (S/TEM) after certain numbers of charge-discharge cycling of the batteries. It is found that structural degradation occurs from the very first cycle and is spatially initiated from the surface of the particle and propagates towards the inner bulk as cyclic number increase, featuring the formation of the surface phase transformation layer and gradual thickening of this layer. The structure degradation is found to follow a sequential phase transformation: monoclinic C2/m → tetragonal I41 → cubic spinel (as shown in Figure 1), which is consistently supported by the decreasing lattice formation energy based on DFT calculations. For the first time, high spatial resolution quantitative chemical analysis reveals that 20% oxygen in the surface phase transformation layer is removed and such newly developed surface layer is a Li-depleted layer with reduced Mn cations (Figure 2). This work demonstrates a direct correlation between structural degradation and cell’s electrochemical degradation. In a more general term, since Li2MnO3 cathode is the parent compound for LMR cathode, this work will enhance our understanding on the degradation mechanism of LMR cathode materials during cycling.

Transformation from monoclinic LiMnO2 to spinel Li xMn2O4 during electrochemical cycling

Structure Change of Orthorhombic LiMnO2cathodes During Electrochemical Cycle for Rechargeable Lithium Battery

Phase Transformations And Activation Characteristics Of Layered Orthorhombic Limno2 During Electrochemical Cycling

Evolutions of Phase and Microstructure of Orthorhombic Li1-xMnO2 (0 <= x <= 0.95) during the First Charge Process

Unusual Spinel-to-Layered Transformation in LiMn 2 O 4 Cathode Explained by Electrochemical and Thermal Stability Investigation.

Synthesis and Electrochemical Properties of LiMn2O4 Spinel Phase with Nanostructure

Effect of Cr doping on LiMnO2

High-performance LiNi0.5Mn1.5O4 spinel controlled by Mn3+ concentration and site disorder.

Tracking the Structural Evolution at Atomic-Scale in the Spinel Mn3o4 Induced by Electrochemical Cycling

Migration of Mn Cations in Delithiated Lithium Manganese Oxides

Correlating Cycle Performance Improvement and Structural Alleviation in LiMn2-xMxO4 Spinel Cathode Materials: A Systematic Study on the Effects of Metal-Ion Doping

Structure Change of Li1.05Ni0.05Mn1.9O4 Cathode Material During Li Extraction

Synthesis and Phase Transition of Li–Mn–O Spinels with High Li/Mn Ratio by Thermo-Decomposition of LiMnC2O4(Ac)

The effect of Na 0.44 MnO 2 formation in Na + -modified spinel LiMn 2 O 4

Phase transformation mechanism in lithium manganese nickel oxide revealed by single-crystal hard X-ray microscopy

Charge-Discharge Cycling Induced Structural and Chemical Evolution of Li2MnO3 Cathode for Li-ion Batteries

Degradation and Structural Evolution Ofxli2mno3·(1–x)limn1/3ni1/3co1/3o2during Cycling

Structural and electrochemical characterization of LiMn2-2xLixNixO4 (0 <= x <= 0.1) cathode materials

Changes in Mn3+/Mn4+ Ratio, Resistance Values in Electrochemical Impedance Spectra, and Rate Capability with Increased Lithium Content in Spinel LixMn2O4

Evolution of Spinel LiMn 2 O 4 Single Crystal Morphology Induced by the Li 2 MnO 3 Phase during Sintering

Structure of Electrochemically Lithiated Li_（0.33）MnO_2