Abstract:Graphitic carbons with ordered mesostructure and high surface areas (of great interest in applications such as energy storage) have been synthesized by a direct triblock‐copolymer‐templating method. Pluronic F127 is used as a structure‐directing agent, with a low‐molecular‐weight phenolic resol as a carbon source, ferric oxide as a catalyst, and silica as an additive. Inorganic oxides can be completely eliminated from the carbon. Small‐angle XRD and N2 sorption analysis show that the resultant carbon materials possess an ordered 2D hexagonal mesostructure, uniform bimodal mesopores (about 1.5 and 6 nm), high surface area (∼1300 m2/g), and large pore volumes (∼1.50 cm3/g) after low‐temperature pyrolysis (900 °C). All surface areas come from mesopores. Wide‐angle XRD patterns demonstrate that the presence of the ferric oxide catalyst and the silica additive lead to a marked enhancement of graphitic ordering in the framework. Raman spectra provide evidence of the increased content of graphitic sp2 carbon structures. Transmission electron microscopy images confirm that numerous domains in the ordered mesostructures are composed of characteristic graphitic carbon nanostructures. The evolution of the graphitic structure is dependent on the temperature and the concentrations of the silica additive, and ferric oxide catalyst. Electrochemical measurements performed on this graphitic mesoporous carbon when used as an electrode material for an electrochemical double layer capacitor shows rectangular‐shaped cyclic voltammetry curves over a wide range of scan rates, even up to 200 mV/s, with a large capacitance of 155 F/g in KOH electrolyte. This method can be widely applied to the synthesis of graphitized carbon nanostructures.

Direct Triblock-Copolymer-Templating Synthesis of Highly Ordered Fluorinated Mesoporous Carbon

Fluorinated Carbon with Ordered Mesoporous Structure.

An Aqueous Cooperative Assembly Route to Synthesize Ordered Mesoporous Carbons with Controlled Structures and Morphology

Facile Synthesis of Ordered Mesoporous Carbons with High Thermal Stability by Self-Assembly of Resorcinol-Formaldehyde and Block Copolymers under Highly Acidic Conditions

Synthesis of Partially Graphitic Ordered Mesoporous Carbons with High Surface Areas

A facile aqueous route tosynthesize highly ordered mesoporous carbons with open pore structures

Synthesis of Ordered Mesoporous Carbon with Dual Templates As Structure Directing Agents

Synthesis of ultra-large mesoporous carbons from triblock copolymers and phloroglucinol/formaldehyde polymer

Direct synthesis of ordered mesoporous carbons.

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Highly Ordered Mesoporous Carbonaceous Frameworks from a Template of a Mixed Amphiphilic Triblock-Copolymer System of PEO-PPO-PEO and Reverse PPO-PEO-PPO.

Design of Amphiphilic ABC Triblock Copolymer for Templating Synthesis of Large-Pore Ordered Mesoporous Carbons with Tunable Pore Wall Thickness

The Structural Optimization and High Electrochemical Behavior of Porous Carbons by Graphitization in Molten Sodium Metals

Kilogram-scale synthesis of ordered mesoporous carbons and their electrochemical performance

Controlled synthesis and functionalization of ordered large-pore mesoporous carbons

Ordered Mesoporous Carbon Prepared from Triblock Copolymer/Novolac Composites

Synthesis and Characterization of Ordered Mesoporous Carbon Using a Novel Carbon Precursor

Thick Wall Mesoporous Carbons with a Large Pore Structure Templated from a Weakly Hydrophobic PEO–PMMA Diblock Copolymer

Design of Carbon Materials with Ultramicro-, Supermicro- and Mesopores Using Solvent- and Self-Template Strategy for Supercapacitors

Study on experiment of synthesis of ordered mesoporous carbon materials doped with fluorine and nitrogen

Ordered Mesoporous Carbon Materials Synthesized by Organic-Organic Self-Assembly