Abstract:Mixed amphiphilic block copolymers of poly(ethylene oxide)-poly(propylene oxide)-poly(ethylene oxide) (PEO–PPO–PEO) and polydimethylsiloxane-poly(ethylene oxide) (PDMS–PEO) have been successfully used as co-templates to prepare ordered mesoporous polymer–silica and carbon–silica nanocomposites by using phenolic resol polymer as a carbon precursor via the strategy of evaporation-induced self-assembly (EISA). The ordered mesoporous materials of 2-D hexagonal (p6m) mesostructures have been achieved, as confirmed by small-angle X-ray scattering (SAXS), transmission electron microscopy (TEM), and nitrogen-sorption measurements. Experiments show that using PDMS–PEO as co-template can enlarge the pore sizes and reduce the framework shrinkage of the materials without evident effect on the specific surface areas. Ordered mesoporous carbons can then be obtained with large pore sizes of 6.7 nm, pore volumes of 0.52 cm3/g, and high surface areas of 578 m2/g. The mixed micelles formed between the hydrophobic PDMS groups and the PPO chains of the F127 molecules should be responsible for the variation of the pore sizes of the resulting mesoporous materials. Through the study of characteristics of mesoporous carbon and mesoporous silica derived from mother carbon–silica nanocomposites, we think mesoporous carbon–silica nanocomposites with the silica-coating mesostructure can be formed after the pyrolysis of the PDMS–PEO diblock copolymer during surfactant removal process. Such method can be thought as the combination of surfactant removal and silica incorporation into one-step. This simple one-pot route provides a pathway for large-scale convenient synthesis of ordered mesostructured nanocomposite materials.

Design of Amphiphilic ABC Triblock Copolymer for Templating Synthesis of Large-Pore Ordered Mesoporous Carbons with Tunable Pore Wall Thickness

Large-Pore Ordered Mesoporous Carbons with Tunable Structures and Pore Sizes Templated from Poly(Ethylene Oxide)-B-Poly(Methyl Methacrylate)

Ordered Mesoporous Silicas And Carbons With Large Accessible Pores Templated From Amphiphilic Diblock Copolymer Poly(Ethylene Oxide)-B-Polystyrene

Highly Ordered Mesoporous Carbonaceous Frameworks from a Template of a Mixed Amphiphilic Triblock-Copolymer System of PEO-PPO-PEO and Reverse PPO-PEO-PPO.

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

Thick Wall Mesoporous Carbons with a Large Pore Structure Templated from a Weakly Hydrophobic PEO–PMMA Diblock Copolymer

Structure design of mesoporous carbons by blending PEO–PPO–PEO-type and PPO–PEO–PPO-type amphiphilic block copolymers in organic–organic self-assembly

Ultra-large-pore mesoporous carbons templated from polyethylene oxide-b-polystyrene diblock copolymer by adding polystyrene homopolymer as a pore expander

Worm-Hole Structured Mesoporous Carbon Monoliths Synthesized with Amphiphilic Triblock Copolymer

Ordered Nanoporous Carbons with Broadly Tunable Pore Size Using Bottlebrush Block Copolymer Templates

Progress on the Fabrication of Ordered Mesoporous Materials with Large Pores by Using Novel Amphiphilic Block Copolymers As Templates

Triconstituent Co-Assembly to Ordered Mesostructured Polymer-Silica and Carbon-Silica Nanocomposites and Large-Pore Mesoporous Carbons with High Surface Areas.

Facile Synthesis of Ordered Mesoporous Carbons with High Thermal Stability by Self-Assembly of Resorcinol-Formaldehyde and Block Copolymers under Highly Acidic Conditions

Preparation of Highly-Ordered Mesoporous Carbons by Organic-Organic Self-Assembly Using the Reverse Amphiphilic Triblock Copolymer PPO–PEO–PPO with a Long Hydrophilic Chain

Synthesis of Well-Defined Microporous Carbons by Molecular-Scale Templating with Polyhedral Oligomeric Silsesquioxane Moieties.

High-Molecular-Weight PLA-b-PEO-b-PLA Triblock Copolymer Templated Large Mesoporous Carbons for Supercapacitors and CO2 Capture

Synthesis of ultra-large mesoporous carbons from triblock copolymers and phloroglucinol/formaldehyde polymer

One-pot Synthesis of Ordered Mesoporous Carbon–silica Nanocomposites Templated by Mixed Amphiphilic Block Copolymers

An Aqueous Cooperative Assembly Route to Synthesize Ordered Mesoporous Carbons with Controlled Structures and Morphology

Template Synthesis of Large Pore Ordered Mesoporous Carbon

Large-pore Ordered Mesoporous Materials Templated from Non-Pluronic Amphiphilic Block Copolymers.