Abstract:This work demonstrated the combination of the self-assembly of a block copolymer with the well-established non-solvent induced phase separation process. Nanoporous films were obtained with well-ordered cylinder pores perpendicular to the film surfaces on top of a non-ordered bicontinous porous layer. Numerous parameters during the film formation process, including the concentration of casting solution, the solvent evaporation time, the temperature of precipitation bath, and the gate height of doctor blade, were systematically investigated to realize the effective control of surface morphology. Voronoi tessellation was first introduced to quantitatively describe the regularity of the surface pattern. It was found that the concentration of casting solution and the solvent evaporation time have synergetic influences on the porous structures. With the increase of concentration, the minimum evaporation time needed for a well-ordered porous surface decreases. If keep the concentration as a constant, the evolution of surface morphologies from non-ordered cylinder pores to ordered cylinder pores, and then to lamellar pores, was observed with the increase of evaporation time. Although lots of combinations of these two parameters can be utilized for the well-ordered structure formation, the mean pore size of the film surface didn't change significantly with the change of film preparation conditions. Besides, the decrease of the temperature of precipitation bath also helped to improve surface pattern regularity. Further study revealed that once the gate height of casting solution was decreased, the evaporation of solvent induced more significant change of casting solution concentration and the solvent composition, resulting in the disappearance of well-ordered cylinder pores. Two ways, including decreasing the solvent evaporation time and applying the solvent annealing process, were proven to be very effective to prepare thinner films with well-ordered nanoporous structures. The above results greatly broaden the operation window and provide possibilities to fabricate films suitable for different applications.

Direct Synthesis of Ordered Mesoporous Polymer/Carbon Nanofilaments with Controlled Mesostructures

Synthesis and Characterisation of Ordered Arrays of Mesoporous Carbon Nanofibres

Direct Synthesis of Mesoporous Carbon Microwires and Nanowires

Facile Synthesis of Ordered Mesoporous Carbons with High Thermal Stability by Self-Assembly of Resorcinol-Formaldehyde and Block Copolymers under Highly Acidic Conditions

A Family of Highly Ordered Mesoporous Polymer Resin and Carbon Structures from Organic−Organic Self-Assembly

Challenges in fabrication of mesoporous carbon films with ordered cylindrical pores via phenolic oligomer self-assembly with triblock copolymers.

Preparation of Free-Standing High Quality Mesoporous Carbon Membranes

Morphology control in mesoporous carbon films using solvent vapor annealing

Triconstituent Co-Assembly to Ordered Mesostructured Polymer-Silica and Carbon-Silica Nanocomposites and Large-Pore Mesoporous Carbons with High Surface Areas.

Nanoporous nonwoven fibril-like morphology by cooperative self-assembly of poly(ethylene oxide)-block-poly(ethyl acrylate)-block-polystyrene and phenolic resin

An Aqueous Cooperative Assembly Route to Synthesize Ordered Mesoporous Carbons with Controlled Structures and Morphology

Preparation of Aluminosilicate Ferrierite Zeolite Nanosheets with Controllable Thickness in the Presence of a Sole Organic Structure Directing Agent

Morphological control of highly ordered mesoporous carbon

Highly Ordered Mesoporous Carbonaceous Frameworks from a Template of a Mixed Amphiphilic Triblock-Copolymer System of PEO-PPO-PEO and Reverse PPO-PEO-PPO.

Direct Triblock-Copolymer-Templating Synthesis of Highly Ordered Fluorinated Mesoporous Carbon

Direct Triblock-Copolymer-templating Synthesis of Ordered Nitrogen-Containing Mesoporous Polymers.

Ordered mesoporous polymers and polymer-silica anocomposites

Preparation and Morphology Control of Highly Ordered Nanoporous Films from Block Copolymers

Conducting polymer and carbon mesoporous structures by electrochemical syntheses

Facile Synthesis of Hierarchically Porous Carbons from Dual Colloidal Crystal/Block Copolymer Template Approach

General Synthesis of Ordered Mesoporous Carbonaceous Hybrid Nanostructures with Molecularly Dispersed Polyoxometallates