Abstract:Block copolymers have long been studied for their theories and applications especially in nanotechnology.1-5 They have periodic structures with 10-100 nm long microphase separated domains which can be controlled by the molecular weight and composition of the block copolymer. Regulating these two parameters, one can prepare thin films with different morphologies over large areas. The patterns formed by the diblock copolymers could be used as templates for structures on the scale of tens to hundreds of nanometers. For the exploitation of block copolymer thin films especially in nanotechnology, the nanopatterns of films with perfectly ordered domains over large areas are prerequisite; therefore, many efforts are focused on controlling the orientation and perfection of ordering of the domains in thin films.6 Interfacial energies7-11 and commensurability12,13 determine the behavior of block copolymer thin films. Thus, changing interfacial energies is a general approach for preparing block copolymer films with perfect ordered domains. For instance, Russell and co-workers used random copolymer brushes to tune the interactions of symmetric and asymmetric polystyrene-b-poly(methyl methacrylate) (PS-b-PMMA) copolymers with their boundaries to achieve perpendicular orientation of domains in thin block copolymer films,5,14 and this way is usually combined with electric fields.14d Electric fields were used to overcome interfacial interactions to orient nanoscopic domains within diblock copolymer films.15 Rockford et al. and Yang et al. employed chemically heterogeneous substrates to control nanoscale surface interactions and subsequent macromolecular ordering.6,16 Segalman et al. demonstrated graphoepitaxy to produce thin film arrays of spherical block copolymer with good long-range order.17 Fasolka et al. reported the use of the dependence of morphologies on the film thickness together with corrugated substratesbywhichthe lateralnanometerscalepatterning of diblock copolymer films was gained.18 Spatz et al. demonstrated the formation of surface-induced nanopattern in ultrathin polystyrene-b-poly(2-vinylpyridine) (PS-bP2VP) films caused by strong adsorption of one of the two blocks forming a quasi-two-dimensional coil while the other block dewets this adsorption layer.19,20 All the above routes obtaining laterally ordered microdomain structures in thin polymer films need thermal treatment. Recently, other nonequilibrium ways have been noted. The adsorption of diblock copolymers from a selective solvent onto a flat solid substrate results in the formation of laterally ordered microdomains.21-24 Apart from these, the solvent-influenced ordering has been used

Preparation and Morphology Control of Highly Ordered Nanoporous Films from Block Copolymers

Directed Self-Assembly of Hierarchical Supramolecular Block Copolymer Thin Films on Chemical Patterns

Controlling Pore Size and Wettability of A Unique Microheterogeneous Copolymer Film with Porous Structure

Controllable Preparation of Block Copolymer Films with Self- Organized Patterns for the Template of Closely - Spaced Nanoparticle Array Formation

Morphology Control of Perpendicularly Oriented Lamellar Films from Azobenzene-Containing Block Copolymers with Different Spacer Lengths

Lateral Nanopatterns in Thin Diblock Copolymer Films Induced by Selective Solvents.

Morphology Controlled Growth of Large Area Ordered Porous Film

Nanoporous nonwoven fibril-like morphology by cooperative self-assembly of poly(ethylene oxide)-block-poly(ethyl acrylate)-block-polystyrene and phenolic resin

Porous Films from Cyclic Block Copolymers

Tunable Assembly of Nanoparticles on Patterned Porous Film.

Membranes with Highly Ordered Straight Nanopores by Selective Swelling of Fast Perpendicularly Aligned Block Copolymers

Fabrication Of Ordered Porous Polymer Film Via A One-Step Strategy And Its Formation Mechanism

Subnanometer porous thin films by the co-assembly of nanotube subunits and block copolymers.

Microphase Separation of Block Copolymer Thin Films.

Well-ordered Self-Assembled Nanostructures of Block Copolymer Films Via Synergistic Integration of Chemoepitaxy and Zone Annealing

Morphology control in mesoporous carbon films using solvent vapor annealing

Preparation of long-range ordered nanostructures in semicrystalline diblock copolymer thin films using micromolding

Surface Morphology Evolution of Poly (Styrene-Block-4-vinylpyridine) (Ps-B-p4vp)(h+) and Poly(Methyl Methacrylate)-Dibenzo-18-Crown-6-Poly(Methyl Methacrylate) (pmcma) Supramolecular Film

Templated self-assembly of block copolymers and morphology transformation driven by the Rayleigh instability

Highly Oriented and Ordered Microstructures in Block Copolymer Films

Synthesis of a Large-Scale Highly Ordered Porous Carbon Film by Self-Assembly of Block Copolymers