Synthesis and Characterization of Ordered Mesoporous Carbon Using a Novel Carbon Precursor
LIU Panbo,JIAO Jian,HUANG Ying,WU Guangli,LIU Peng
DOI: https://doi.org/10.3969/j.issn.1005-023x.2012.14.003
2012-01-01
Abstract:Mesoporous carbon framework with two-dimensional hexagonal structure and worm-like structure were synthesized through organic-organic self-assembly method,by using triblock copolymer F127,P123 and F127/P123 as template and linear phenolic resin as carbon precursor.The structure of ordered mesoporous carbon was cha-racterized by FT-IR,X-ray diffraction,transmission electron microscopy,N2 adsorption/desorption,thermogravime-tric analysis and elemental analyse measurements.The effect of different templates on the structure of mesoporous carbon were investigated.The results showed that mesoporous carbon with two-dimensional hexagonal structure could be synthesized by using F127 as template,and the specific surface areas,the micropore surface areas,the pore vo-lumes,the pore size and the pore wall thickness were 670m2/g,368m2/g,0.40cm3/g,3.2nm and 4.5nm,respectively.The mesoporous carbon with worm-like structure could be synthesized by using P123 as template,and the specific surface areas,the micropore surface areas,the pore volumes and the pore size were 506m2/g,251m2/g,0.27cm3/g and 3.0nm.The pore size of mesoporous carbons prepared from F127/P123 were larger than that of mesoporous carbon prepared from single template,and the specific surface areas,the micropore surface areas,the pore sizes,the pore volumes and the pore wall thicknesses reduced with the mass fraction of F127 decreasing.