EFFECT OF GLASS FRIT WETTING PROPERTY ON THE PERFORMANCES OF SILICON SOLAR CELLS

Yaping ZHANG,Yunxia YANG,Jianhua ZHENG,Lihua DING,Wei HUA,Guorong CHEN

DOI: https://doi.org/10.3321/j.issn:0454-5648.2008.07.027

2008-01-01

Abstract:PbO-Al2O3- B2O3-SiO2 glass frits were used as binders during rapid thermal processing (RTP) for manufacturing Si solar cells. The influences of the PbO-Al2O3- B2O3-SiO2 glass frit wetting property on the Ag/Si ohmic contact, sintering of Ag powder particles and conducting mechanism of the Ag grid were discussed. The softening temperatures were determined by the viscosity-temperature curves, which were measured through parallel plate viscometry. Scanning electron microscopy was used for investigating the microstructures of the surfaces of the Ag grids. The series resistance, fill factor, open circuit voltage and efficiency were determined by I-V analysis. The results show that good wetting ability can improve the sintering of Ag powders because the lower the softening temperature, the denser the structure of the Ag grid. The wetting ability affects the conducting mechanism as well as the amount and size of Ag re-crystallites, which form Ag/Si contacts. Therefore, glass frit with proper wetting ability is a key factor to obtain the best performance of solar cells.