Preparation, Magnetic And Transport Properties Of La0.75na0.25mno3 Epitaxial Film

Han Li-An,Meng Quan-Shui,Chang Lin,Liao Shao-Jun,Chen Chang-Le

DOI: https://doi.org/10.3724/SP.J.1077.2008.00683

IF: 1.292

2008-01-01

Journal of Inorganic Materials

Abstract:Using RF magnetron sputtering method, La0.75Na0.25MnO3 film with thickness of 120nm was epitaxially grown on (100) LaAlO3 single-crystal substrate. The thin film was characterized by X-ray diffraction, Superconducting quantum interference device and DC four probed method. The results indicate that the thin film shows a well epitaxial direction of (100) and the Curie temperature is 270K. Near the Curie temperature, the magnetic property shows a transition from ferromagnetic to paramagnetic character. La0.75Na0.25MnO3 thin film exhibits a characteristic spin glass state, which is due to strain effect. The thin film exhibits a quite distinctive magnetoresistance effect which is 40.3% near the Curie temperature when the magnetic field is IT. Transport properties indicate that the resistivity satisfies the formula of rho = rho(0) - rho T-1(2) + rho T-2(5) from 80K to 210K which is due to electron-electron scattering, the resistivity satisfies phase separate percolation model from 220K to T-MI, the resistivity satisfies polarons model when the temperature is above T-MI which is due to the existence of the small polarons nearest hopping.