Abstract:The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime Up to 10(7) cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AISI 4340 steel in which the inclusion size is smaller than 5.5 mu m, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 mu m, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 mu m. In the case of internal inclusion-induced fractures at cycles beyond about 1x10(6) for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure N-f in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with N-f, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1x10(6). Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.

Effect of Inclusion Size on High-Cycle Fatigue Behavior of High Strength Spring Steel

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

Influence of Inclusion Size on Fatigue Behavior of High Strength Steels in the Gigacycle Fatigue Regime

High-Cycle Fatigue Properties of 60Si2CrVA Spring Steels Produced by Two Different Metallurgical Processes

Variation In Mechanical Properties, Microstructures And Fracture Behavior Of 304 Stainless Steel During Low-Cycle Fatigue

Multi-scale Deformation Behavior Investigation of 18cr–8ni Austenitic Steel Subjected to Low-Cycle Fatigue Loading

Ultra High Cycle Fatigue Behavior of Automotive High Strength Spring Steels 54sicrv6 and 54Sicr6

The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42crmovnb Steel

Fatigue fracture behaviour of a medium-carbon 2 000 MPa level high strength spring steel

Gigacycle Fatigue Behavior of 1800 MPa Grade High Strength Spring Steel for Automobile Lightweight

Dependence of Fatigue Strength on Inclusion Size for High-Strength Steels in Very High Cycle Fatigue Regime

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

Effects of inclusion size and stress ratio on the very-high-cycle fatigue behavior of pearlitic steel

Very High Cycle Fatigue Behaviour of 2000‐mpa Ultra‐high‐strength Spring Steel with Bainite–martensite Duplex Microstructure

Ultra high cycle fatigue behavior of a medium-carbon high strength spring steel NHS1

Ultra-high Cycle Fatigue Fracture Mechanism of a Precipitation HardeningStainless Steel at Different Stress Ratios

Relationship among Fatigue Life, Inclusion Size and Hydrogen Concentration for High-Strength Steel in the VHCF Regime

Failure Behavior of Ultra-high Cycle Fatigue of a 2 000 MPa Grade High Strength Steel

High-cycle Bending Fatigue Behaviour of Nanostructured Bainitic Steel

Effect of Inclusion Size and Distribution on Low Cycle Fatigue Properties of an FGH97 Superalloy