Abstract:The fatigue fracture behavior of four ultrahigh strength steels with different melting processes and therefore different inclusion sizes were studied by using a rotating bar two-point bending fatigue machine in the high-cycle regime Up to 10(7) cycles of loading. The fracture surfaces were observed by field emission scanning electron microscopy (FESEM). It was found that the size of inclusion has significant effect on the fatigue behavior. For AISI 4340 steel in which the inclusion size is smaller than 5.5 mu m, all the fatigue cracks except one did not initiated from inclusion but from specimen surface and conventional S-N curve exists. For 65Si2MnWE and Aermet 100 steels in which the average inclusion sizes are 12.2 and 14.9 mu m, respectively, fatigue cracks initiated from inclusions at lower stress amplitudes and stepwise S-N curves were observed. The S-N curve displays a continuous decline and fatigue failures originated from large oxide inclusion for 60Si2CrVA steel in which the average inclusion size is 44.4 mu m. In the case of internal inclusion-induced fractures at cycles beyond about 1x10(6) for 65Si2MnWE and 60Si2CrVA steels, inclusion was always found inside the fish-eye and a granular bright facet (GBF) was observed in the vicinity around the inclusion. The GBF sizes increase with increasing the number of cycles to failure N-f in the long-life regime. The values of stress intensity factor range at crack initiation site for the GBF are almost constant with N-f, and are almost equal to that for the surface inclusion and the internal inclusion at cycles lower than about 1x10(6). Neither fish-eye nor GBF was observed for Aermet 100 steel in the present study.

Effects of inclusion size and stress ratio on the very-high-cycle fatigue behavior of pearlitic steel

Influence of Inclusion Size on Fatigue Behavior of High Strength Steels in the Gigacycle Fatigue Regime

Effects of low-cycle fatigue on static mechanical properties, microstructures and fracture behavior of 304 stainless steel

The Effect of Inclusions on the Fatigue Behavior of Fine-Grained High Strength 42crmovnb Steel

Fatigue hardening/softening behaviour investigated through Vickers microhardness measurement during high-cycle fatigue

Effects of stress ratio on high-cycle and very-high-cycle fatigue behavior of a Ti–6Al–4V alloy

High-Cycle Fatigue Fracture Behavior of Ultrahigh Strength Steels

Effect of Stress Ratio on Very High Cycle Fatigue Properties of Ti-10V-2Fe-3Al Alloy with Duplex Microstructure

Effect of Inclusion Size on High-Cycle Fatigue Behavior of High Strength Spring Steel

Dependence of Fatigue Strength on Inclusion Size for High-Strength Steels in Very High Cycle Fatigue Regime

Non-inclusion induced crack initiation in multiphase high-strength steel during very high cycle fatigue

Effect of stress ratio on long life fatigue behavior of high carbon chromium bearing steel under axial loading

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method

An experimental investigation of fatigue performance and crack initiation characteristics for an SLMed Ti-6Al-4V under different stress ratios up to very-high-cycle regime

The Effect of Stress Ratios on the Very High Cycle Fatigue Behavior of 9%Cr Turbine Steel at 630 °C

Effect of stress ratio on VHCF behavior for a compressor blade titanium alloy

Relationship among Fatigue Life, Inclusion Size and Hydrogen Concentration for High-Strength Steel in the VHCF Regime

Failure Behavior of Ultra-high Cycle Fatigue of a 2 000 MPa Grade High Strength Steel

Microstructure-Based Fatigue Modeling with Residual Stresses: Effect of Inclusion Shape on Very High Cycle Fatigue Life

Effect of Inclusion Size and Distribution on Low Cycle Fatigue Properties of an FGH97 Superalloy

Effects of Inclusion and Loading Direction on the Fatigue Behavior of Hot Rolled Low Carbon Steel